Formation of soft magnetic thin films by means of electrochemical methods

Tetsuya Osaka*, Atsushi Sugiyama, Toru Asahi, Jun Kawaji


研究成果: Conference contribution


Development of CoFe soft magnetic thin film for a recording head core and a CoNiFeB soft magnetic underlayer for double-layered perpendicular recording media by means of electrochemical methods are reviewed. The highest B s value of 2.4 T was attained with electrodeposited Co 35Fe65 films by avoiding the formation of Fe3+ in the bath during the electrodeposition. The Hc value lower than 6 Oe was attained with maintaining the Bs at 2.4 T by combining the electrodeposition using pulsed current with a post-annealing process. On the other hand, the CoNiFeB film could be formed on a 2.5 inch-diameter Si single crystal disk with sufficient uniformity. The magnetic domain structure of CoNiFeB was able to be controlled by preparation conditions in electroless deposition, e.g. rotating speed of the disk substrate and application of external magnetic field. Consequently, the CoNiFeB soft magnetic underlayer exhibiting no spike noise could be prepared by optimizing these conditions.

ホスト出版物のタイトルMagnetic Materials, Processes, and Devices VIII - Proceedings of the International Symposium
出版ステータスPublished - 2006
イベント206th ECS Meeting - Honolulu, HI, United States
継続期間: 2004 10月 52004 10月 8


名前Proceedings - Electrochemical Society
PV 2004-23


Conference206th ECS Meeting
国/地域United States
CityHonolulu, HI

ASJC Scopus subject areas

  • 工学(全般)


「Formation of soft magnetic thin films by means of electrochemical methods」の研究トピックを掘り下げます。これらがまとまってユニークなフィンガープリントを構成します。