Highly spin-polarized Co2MnGa0.5Sn0.5 Heusler compound

B. S.D.Ch S. Varaprasad, A. Rajanikanth, Y. K. Takahashi, K. Hono*

*この研究の対応する著者

研究成果: Article査読

46 被引用数 (Scopus)

抄録

Point contact Andreev reflection measurements of Co2MnSn1-xGax alloys showed that the spin polarization of L21 ordered quaternary Co2MnSn0.5Ga0.5 compound increased to 0.72 compared to 0.6 for Co2MnSn and Co2MnGa ternary alloys. The L21 Co2MnSn0.5Ga0.5 phase was found to be an intermetallic compound, in which the L21 structure was stable up to the melting temperature. The increase in spin polarization was attributed to the high degree of L21 order as well as an increase in the spin-up density of states near the Fermi level.

本文言語English
ページ(範囲)2702-2709
ページ数8
ジャーナルActa Materialia
57
9
DOI
出版ステータスPublished - 2009 5
外部発表はい

ASJC Scopus subject areas

  • 電子材料、光学材料、および磁性材料
  • セラミックおよび複合材料
  • ポリマーおよびプラスチック
  • 金属および合金

フィンガープリント

「Highly spin-polarized Co<sub>2</sub>MnGa<sub>0.5</sub>Sn<sub>0.5</sub> Heusler compound」の研究トピックを掘り下げます。これらがまとまってユニークなフィンガープリントを構成します。

引用スタイル