Hydrogen embrittlement of work-hardened Ni-Ti alloy in fluoride solutions

Ken'ichi Yokoyama*, Kazuyuki Kaneko, Toshio Ogawa, Keiji Moriyama, Kenzo Asaoka, Jun'Ichi Sakai

*この研究の対応する著者

    研究成果: Article査読

    54 被引用数 (Scopus)

    抄録

    Hydrogen embrittlement of work-hardened Ni-Ti alloy has been examined in acidulated phosphate fluoride (APF) solutions. Upon immersion in a 2.0% APF solution with a pH of 5.0, tensile strength decreased markedly with immersion time. Moreover, the fracture mode changed from ductile to brittle due to brittle layer formation at the peripheral part of the cross section of the specimen. The amount of absorbed hydrogen increased linearly with immersion time, and it reached above 5000 mass ppm after 24h. The hydrogen desorption temperature of the immersed specimens shifted from 450°C to a lower temperature with immersion time. As the amount of absorbed hydrogen was larger than 500 mass ppm, the degradation of mechanical properties was recognized. Although the tensile properties and fracture mode scarcely change in a 0.2% APF solution, the slight reduction in hardness and hydrogen absorption of several hundreds mass ppm were observed. The results of the present study imply that work-hardened Ni-Ti alloy is less sensitive to hydrogen embrittlement compared with Ni-Ti superelastic alloy.

    本文言語English
    ページ(範囲)101-108
    ページ数8
    ジャーナルBiomaterials
    26
    1
    DOI
    出版ステータスPublished - 2005 1月

    ASJC Scopus subject areas

    • バイオテクノロジー
    • バイオエンジニアリング
    • 生体医工学

    フィンガープリント

    「Hydrogen embrittlement of work-hardened Ni-Ti alloy in fluoride solutions」の研究トピックを掘り下げます。これらがまとまってユニークなフィンガープリントを構成します。

    引用スタイル