Impurity diffusion measurements of Bi in liquid Sn using stable density layering and the shear cell technique

Shinsuke Suzuki, Kurt Helmut Kraatz, Günter Frohberg, Raluca Roşu-Pflumm, German Müller-Vogt

研究成果: Article

9 引用 (Scopus)

抄録

To obtain reliable diffusion data on earth, impurity diffusion experiments of Bi in liquid Sn were performed using a stable density layering and the shear cell technique with a reservoir system to provide pressure on the liquid. The experiment type was diffusion of Bi from a SnBi3at.% (5 wt%) thick layer into Sn. The diffusion temperatures (diffusion times) were 300 °C (8 h), 500 °C (4.5 h) and 800 °C (2.5 h). At each temperature four parallel experiments were performed simultaneously in one shear cell cartridge. After the diffusion experiments, the Bi concentration profiles were measured by atom absorption spectroscopy. The diffusion coefficients were determined by fitting with the thick layer solution considering the correction method of the shear convection and the averaging effect. As a result, the concentration profiles had only small deviations and the diffusion coefficients agreed well among the four parallel experiments. The mean diffusion coefficient at 300 °C agreed well with data from the 1g-diffusion experiments in a magnetic field and with μg-data. It was also shown that this method can be applied also to interdiffusion experiments, in which the influence of Marangoni convection can be investigated by the variation of the pressure inside the capillary and artificial free surfaces on the liquid sample. The temperature dependence of the diffusion coefficient was empirically described as the nth power law (n ≈ 1.8) of T.

元の言語English
ページ(範囲)3300-3304
ページ数5
ジャーナルJournal of Non-Crystalline Solids
353
発行部数32-40
DOI
出版物ステータスPublished - 2007 10 15
外部発表Yes

Fingerprint

Impurities
shear
impurities
Liquids
liquids
cells
diffusion coefficient
Experiments
Marangoni convection
cartridges
profiles
absorption spectroscopy
convection
deviation
Absorption spectroscopy
temperature dependence
Temperature
temperature
magnetic fields
Earth (planet)

ASJC Scopus subject areas

  • Ceramics and Composites
  • Electronic, Optical and Magnetic Materials

これを引用

Impurity diffusion measurements of Bi in liquid Sn using stable density layering and the shear cell technique. / Suzuki, Shinsuke; Kraatz, Kurt Helmut; Frohberg, Günter; Roşu-Pflumm, Raluca; Müller-Vogt, German.

:: Journal of Non-Crystalline Solids, 巻 353, 番号 32-40, 15.10.2007, p. 3300-3304.

研究成果: Article

Suzuki, Shinsuke ; Kraatz, Kurt Helmut ; Frohberg, Günter ; Roşu-Pflumm, Raluca ; Müller-Vogt, German. / Impurity diffusion measurements of Bi in liquid Sn using stable density layering and the shear cell technique. :: Journal of Non-Crystalline Solids. 2007 ; 巻 353, 番号 32-40. pp. 3300-3304.
@article{72e12473bf024bf488400dce0e295410,
title = "Impurity diffusion measurements of Bi in liquid Sn using stable density layering and the shear cell technique",
abstract = "To obtain reliable diffusion data on earth, impurity diffusion experiments of Bi in liquid Sn were performed using a stable density layering and the shear cell technique with a reservoir system to provide pressure on the liquid. The experiment type was diffusion of Bi from a SnBi3at.{\%} (5 wt{\%}) thick layer into Sn. The diffusion temperatures (diffusion times) were 300 °C (8 h), 500 °C (4.5 h) and 800 °C (2.5 h). At each temperature four parallel experiments were performed simultaneously in one shear cell cartridge. After the diffusion experiments, the Bi concentration profiles were measured by atom absorption spectroscopy. The diffusion coefficients were determined by fitting with the thick layer solution considering the correction method of the shear convection and the averaging effect. As a result, the concentration profiles had only small deviations and the diffusion coefficients agreed well among the four parallel experiments. The mean diffusion coefficient at 300 °C agreed well with data from the 1g-diffusion experiments in a magnetic field and with μg-data. It was also shown that this method can be applied also to interdiffusion experiments, in which the influence of Marangoni convection can be investigated by the variation of the pressure inside the capillary and artificial free surfaces on the liquid sample. The temperature dependence of the diffusion coefficient was empirically described as the nth power law (n ≈ 1.8) of T.",
keywords = "Diffusion and transport, Liquid alloys and liquid metals, Measurement techniques",
author = "Shinsuke Suzuki and Kraatz, {Kurt Helmut} and G{\"u}nter Frohberg and Raluca Roşu-Pflumm and German M{\"u}ller-Vogt",
year = "2007",
month = "10",
day = "15",
doi = "10.1016/j.jnoncrysol.2007.05.075",
language = "English",
volume = "353",
pages = "3300--3304",
journal = "Journal of Non-Crystalline Solids",
issn = "0022-3093",
publisher = "Elsevier",
number = "32-40",

}

TY - JOUR

T1 - Impurity diffusion measurements of Bi in liquid Sn using stable density layering and the shear cell technique

AU - Suzuki, Shinsuke

AU - Kraatz, Kurt Helmut

AU - Frohberg, Günter

AU - Roşu-Pflumm, Raluca

AU - Müller-Vogt, German

PY - 2007/10/15

Y1 - 2007/10/15

N2 - To obtain reliable diffusion data on earth, impurity diffusion experiments of Bi in liquid Sn were performed using a stable density layering and the shear cell technique with a reservoir system to provide pressure on the liquid. The experiment type was diffusion of Bi from a SnBi3at.% (5 wt%) thick layer into Sn. The diffusion temperatures (diffusion times) were 300 °C (8 h), 500 °C (4.5 h) and 800 °C (2.5 h). At each temperature four parallel experiments were performed simultaneously in one shear cell cartridge. After the diffusion experiments, the Bi concentration profiles were measured by atom absorption spectroscopy. The diffusion coefficients were determined by fitting with the thick layer solution considering the correction method of the shear convection and the averaging effect. As a result, the concentration profiles had only small deviations and the diffusion coefficients agreed well among the four parallel experiments. The mean diffusion coefficient at 300 °C agreed well with data from the 1g-diffusion experiments in a magnetic field and with μg-data. It was also shown that this method can be applied also to interdiffusion experiments, in which the influence of Marangoni convection can be investigated by the variation of the pressure inside the capillary and artificial free surfaces on the liquid sample. The temperature dependence of the diffusion coefficient was empirically described as the nth power law (n ≈ 1.8) of T.

AB - To obtain reliable diffusion data on earth, impurity diffusion experiments of Bi in liquid Sn were performed using a stable density layering and the shear cell technique with a reservoir system to provide pressure on the liquid. The experiment type was diffusion of Bi from a SnBi3at.% (5 wt%) thick layer into Sn. The diffusion temperatures (diffusion times) were 300 °C (8 h), 500 °C (4.5 h) and 800 °C (2.5 h). At each temperature four parallel experiments were performed simultaneously in one shear cell cartridge. After the diffusion experiments, the Bi concentration profiles were measured by atom absorption spectroscopy. The diffusion coefficients were determined by fitting with the thick layer solution considering the correction method of the shear convection and the averaging effect. As a result, the concentration profiles had only small deviations and the diffusion coefficients agreed well among the four parallel experiments. The mean diffusion coefficient at 300 °C agreed well with data from the 1g-diffusion experiments in a magnetic field and with μg-data. It was also shown that this method can be applied also to interdiffusion experiments, in which the influence of Marangoni convection can be investigated by the variation of the pressure inside the capillary and artificial free surfaces on the liquid sample. The temperature dependence of the diffusion coefficient was empirically described as the nth power law (n ≈ 1.8) of T.

KW - Diffusion and transport

KW - Liquid alloys and liquid metals

KW - Measurement techniques

UR - http://www.scopus.com/inward/record.url?scp=34548564084&partnerID=8YFLogxK

UR - http://www.scopus.com/inward/citedby.url?scp=34548564084&partnerID=8YFLogxK

U2 - 10.1016/j.jnoncrysol.2007.05.075

DO - 10.1016/j.jnoncrysol.2007.05.075

M3 - Article

AN - SCOPUS:34548564084

VL - 353

SP - 3300

EP - 3304

JO - Journal of Non-Crystalline Solids

JF - Journal of Non-Crystalline Solids

SN - 0022-3093

IS - 32-40

ER -