Intrinsic hard magnetic properties of Sm(Fe,Co)12−xTix compound with ThMn12 structure

A. Makurenkova, D. Ogawa, P. Tozman, S. Okamoto, S. Nikitin, S. Hirosawa, K. Hono, Y. K. Takahashi*

*この研究の対応する著者

研究成果: Article査読

抄録

Sm1.1(Fe0.8Co0.2)12-xTix thin films were grown epitaxially with various Ti contents (x = 0, 0.4, 0.6, 0.9, and 1) to investigate the effects of Ti on the intrinsic hard magnetic properties and phase stability. A single ThMn12-type structure with the (001) texture was obtained for x up to 0.9. A further increase in the Ti content led to a multiphase structure in the Sm1.1(Fe0.8Co0.2)11Ti1 film; this was in contrast to the behavior in the bulk, where x = 1 is necessary to form a single ThMn12-type structure. Meanwhile, increasing the Ti content from x = 0–0.6 in the Sm1.1(Fe0.8Co0.2)12-xTix thin films decreased the saturation magnetization, anisotropy field, and Curie temperature from 1.84 T to 1.55 T, 12–8.7 T, and 800–730 K, respectively. This thin film model shows that the Sm(Fe0.8Co0.2)12-xTix compounds can compete with Nd2Fe14B at 300 K when phase stabilization is achieved at reduced Ti content, for x ≤ 0.5.

本文言語English
論文番号158477
ジャーナルJournal of Alloys and Compounds
861
DOI
出版ステータスPublished - 2021 4 25
外部発表はい

ASJC Scopus subject areas

  • 材料力学
  • 機械工学
  • 金属および合金
  • 材料化学

フィンガープリント

「Intrinsic hard magnetic properties of Sm(Fe,Co)<sub>12−x</sub>Ti<sub>x</sub> compound with ThMn<sub>12</sub> structure」の研究トピックを掘り下げます。これらがまとまってユニークなフィンガープリントを構成します。

引用スタイル