Kinetic characteristics of electrochemical reduction of SiO2 granules in molten CaCl2

Xiao Yang, Kouji Yasuda, Toshiyuki Nohira, Rika Hagiwara, Takayuki Homma

研究成果: Article

13 引用 (Scopus)

抜粋

The kinetic characteristics of electrochemical reduction of SiO2 granules in molten CaCl2 were investigated to develop a new process for producing solar-grade silicon. The reduction rate was evaluated based on the time dependence of the reduction fractions measured from the growth of the reduced Si layer and the weight change of the samples during electrolysis. The samples were prepared by potentiostatic electrolysis of SiO2 granules in molten CaCl2 at 1123 K. The results indicated that the reduction was fast at the initial stage of electrolysis, and gradually slowed as the reaction progressed. The apparent current density reached 0.7 A cm-2 at the initial stage, which was comparable to the commercial Hall-Héroult process for aluminum production.

元の言語English
ページ(範囲)D3116-D3119
ジャーナルJournal of the Electrochemical Society
161
発行部数7
DOI
出版物ステータスPublished - 2014

ASJC Scopus subject areas

  • Electronic, Optical and Magnetic Materials
  • Renewable Energy, Sustainability and the Environment
  • Surfaces, Coatings and Films
  • Electrochemistry
  • Materials Chemistry

フィンガープリント Kinetic characteristics of electrochemical reduction of SiO<sub>2</sub> granules in molten CaCl<sub>2</sub>' の研究トピックを掘り下げます。これらはともに一意のフィンガープリントを構成します。

  • これを引用