Low temperature Cu–Cu bonding by transient liquid phase sintering of mixed Cu nanoparticles and Sn–Bi eutectic powders

M. Khairi Faiz*, Kazuma Bansho, Tadatomo Suga, Tomoyuki Miyashita, Makoto Yoshida

*この研究の対応する著者

研究成果: Article査読

11 被引用数 (Scopus)

抄録

Fluxless bonding of plateless Cu–Cu substrates at processing temperature lower than 250 °C and low pressure of 0.1 MPa was achieved by transient liquid phase sintering (TLPS) of mixed Cu nanoparticles and Sn–Bi eutectic powders. The effects of mixture composition, and sintering temperature on the shear strength, microstructure, and remelting temperature were investigated. Lowering the sintering temperature of Cu mixed with 65 weight percentage of Sn–Bi (Cu–65SnBi) resulted in decreased shear strength, however, at 200 °C sintering temperature, the obtained highest shear strength was more than 20 MPa. It was found that it is essential to use Cu nanoparticles to accelerate the consumption so that no initial Sn–Bi phases remained after processing. The liquid phase generated at approximately 196 °C during sintering from the reaction between newly formed Cu6Sn5 and Bi-phase was expected to facilitate the densification and strengthening of the joints. Although this newly generated liquid phase was known to solidify as hypereutectic Sn–Bi, by controlling the sintering temperature at 200 °C, the remelting event at 139 °C was not observed by differential scanning calorimetry. It is assumed that the proportion of solidified Sn–Bi eutectic phases in Cu–65SnBi that was sintered at 200 °C were significantly small, hence, when reheated at 150 °C, the obtained shear strength was equivalent to that at room temperature.

本文言語English
ページ(範囲)16433-16443
ページ数11
ジャーナルJournal of Materials Science: Materials in Electronics
28
21
DOI
出版ステータスPublished - 2017 11 1

ASJC Scopus subject areas

  • 電子材料、光学材料、および磁性材料
  • 原子分子物理学および光学
  • 凝縮系物理学
  • 電子工学および電気工学

フィンガープリント

「Low temperature Cu–Cu bonding by transient liquid phase sintering of mixed Cu nanoparticles and Sn–Bi eutectic powders」の研究トピックを掘り下げます。これらがまとまってユニークなフィンガープリントを構成します。

引用スタイル