Low temperature sintering-bonding through in-situ formation of Ag nanoparticles using micro-scaled Ag2O composite paste

Fengwen Mu, Guisheng Zou, Zhenyu Zhao, Aiping Wu, Jiuchun Yan, Y. Norman Zhou

研究成果: Article

2 引用 (Scopus)

抜粋

In order to reduce the cost of using Ag nanoparticle paste as bonding materials in electronic packaging, micro-scaled Ag2O powders were mixed with triethylene glycol (TEG) to form a paste to replace the Ag particle paste. The reaction mechanism of in-situ formation of Ag nanoparticles, the sintering characteristics of micro-Ag2O paste at low temperature, and the bonding of Ag-coated Cu bulks using this paste were investigated. The results reveal that the Ag2O particles in the paste were more easily transformed into Ag nanoparticles than micro-Ag2O itself, and with increasing the sintering temperature, more Ag nanoparticles formed and grew larger by sintering, accompanied with some gaseous products which could escape easily. The effect of sintering-bonding time on the strength of joints fabricated at 250°C under a pressure of 2 MPa was analyzed. The average shear strength of the joints increased with sintering-bonding time and reached about 24 MPa when the sintering-bonding time was 5 min. And the microstructure of the fractured surface and the cross-section of typical joints made at 250°C under 2 MPa were also examined.

元の言語English
ページ(範囲)38-42
ページ数5
ジャーナルHanjie Xuebao/Transactions of the China Welding Institution
34
発行部数4
出版物ステータスPublished - 2013 4 1
外部発表Yes

    フィンガープリント

ASJC Scopus subject areas

  • Mechanics of Materials
  • Mechanical Engineering

これを引用