Magnetic properties of electroless-deposited NiFeB and electrodeposited NiFe alloy thin films

Madoka Takai, Kensuke Kageyama, Sanae Takefusa, Akiyoshi Nakamura, Tetsuya Osaka

研究成果: Article

15 引用 (Scopus)

抄録

The magnetic properties and the structure of electroless-deposited NiFeB films were investigated in comparison with those of electrodeposited NiFe films. The electroless-deposited NiFeB film with 27at% Fe content had the lowest coercivity, Hc, as low as 0.5 Oe with a saturation magnetic flux density, Bs, of 1.0 T. The saturation magnetostriction, λs, and the uniaxial magnetic anisotropy, Hk, were 5.0×10-6 and 10 Oe, respectively, which were larger than those of the conventional, electrodeposited permalloy film. The permeability of as-deposited Ni70Fe27B3 film was 1000 at 1 MHz. In order to improve the permeability, the film was heated at 200 °C in a magnetic field applied in the hard-axis direction to decrease the Hk value, and the permeability became 2000 at 1 MHz. The crystal structure and grain size of NiFeB and NiFe films were investigated by XRD, THEED and TEM. Both films with low Hc had an fcc structure; the grain size of the NiFeB film was smaller than 10 nm, while that of the NiFe film was larger, approximately 20 nm. The results suggested that the electroless-deposited NiFeB film had a larger magnetic anisotropy than the electrodeposited NiFe film. Moreover, the films with Hc less than 10 Oe did not show clear difference between their TEM bright images and THEED patterns.

元の言語English
ページ(範囲)1530-1535
ページ数6
ジャーナルIEICE Transactions on Electronics
E78-C
発行部数11
出版物ステータスPublished - 1995 11

Fingerprint

Magnetic properties
Thin films
Magnetic anisotropy
Transmission electron microscopy
Magnetostriction
Magnetic flux
Coercive force
Crystal structure
Magnetic fields

ASJC Scopus subject areas

  • Electrical and Electronic Engineering

これを引用

Magnetic properties of electroless-deposited NiFeB and electrodeposited NiFe alloy thin films. / Takai, Madoka; Kageyama, Kensuke; Takefusa, Sanae; Nakamura, Akiyoshi; Osaka, Tetsuya.

:: IEICE Transactions on Electronics, 巻 E78-C, 番号 11, 11.1995, p. 1530-1535.

研究成果: Article

Takai, M, Kageyama, K, Takefusa, S, Nakamura, A & Osaka, T 1995, 'Magnetic properties of electroless-deposited NiFeB and electrodeposited NiFe alloy thin films', IEICE Transactions on Electronics, 巻. E78-C, 番号 11, pp. 1530-1535.
Takai, Madoka ; Kageyama, Kensuke ; Takefusa, Sanae ; Nakamura, Akiyoshi ; Osaka, Tetsuya. / Magnetic properties of electroless-deposited NiFeB and electrodeposited NiFe alloy thin films. :: IEICE Transactions on Electronics. 1995 ; 巻 E78-C, 番号 11. pp. 1530-1535.
@article{f3b50b044af6484d8c97ceb8b172d627,
title = "Magnetic properties of electroless-deposited NiFeB and electrodeposited NiFe alloy thin films",
abstract = "The magnetic properties and the structure of electroless-deposited NiFeB films were investigated in comparison with those of electrodeposited NiFe films. The electroless-deposited NiFeB film with 27at{\%} Fe content had the lowest coercivity, Hc, as low as 0.5 Oe with a saturation magnetic flux density, Bs, of 1.0 T. The saturation magnetostriction, λs, and the uniaxial magnetic anisotropy, Hk, were 5.0×10-6 and 10 Oe, respectively, which were larger than those of the conventional, electrodeposited permalloy film. The permeability of as-deposited Ni70Fe27B3 film was 1000 at 1 MHz. In order to improve the permeability, the film was heated at 200 °C in a magnetic field applied in the hard-axis direction to decrease the Hk value, and the permeability became 2000 at 1 MHz. The crystal structure and grain size of NiFeB and NiFe films were investigated by XRD, THEED and TEM. Both films with low Hc had an fcc structure; the grain size of the NiFeB film was smaller than 10 nm, while that of the NiFe film was larger, approximately 20 nm. The results suggested that the electroless-deposited NiFeB film had a larger magnetic anisotropy than the electrodeposited NiFe film. Moreover, the films with Hc less than 10 Oe did not show clear difference between their TEM bright images and THEED patterns.",
author = "Madoka Takai and Kensuke Kageyama and Sanae Takefusa and Akiyoshi Nakamura and Tetsuya Osaka",
year = "1995",
month = "11",
language = "English",
volume = "E78-C",
pages = "1530--1535",
journal = "IEICE Transactions on Electronics",
issn = "0916-8524",
publisher = "Maruzen Co., Ltd/Maruzen Kabushikikaisha",
number = "11",

}

TY - JOUR

T1 - Magnetic properties of electroless-deposited NiFeB and electrodeposited NiFe alloy thin films

AU - Takai, Madoka

AU - Kageyama, Kensuke

AU - Takefusa, Sanae

AU - Nakamura, Akiyoshi

AU - Osaka, Tetsuya

PY - 1995/11

Y1 - 1995/11

N2 - The magnetic properties and the structure of electroless-deposited NiFeB films were investigated in comparison with those of electrodeposited NiFe films. The electroless-deposited NiFeB film with 27at% Fe content had the lowest coercivity, Hc, as low as 0.5 Oe with a saturation magnetic flux density, Bs, of 1.0 T. The saturation magnetostriction, λs, and the uniaxial magnetic anisotropy, Hk, were 5.0×10-6 and 10 Oe, respectively, which were larger than those of the conventional, electrodeposited permalloy film. The permeability of as-deposited Ni70Fe27B3 film was 1000 at 1 MHz. In order to improve the permeability, the film was heated at 200 °C in a magnetic field applied in the hard-axis direction to decrease the Hk value, and the permeability became 2000 at 1 MHz. The crystal structure and grain size of NiFeB and NiFe films were investigated by XRD, THEED and TEM. Both films with low Hc had an fcc structure; the grain size of the NiFeB film was smaller than 10 nm, while that of the NiFe film was larger, approximately 20 nm. The results suggested that the electroless-deposited NiFeB film had a larger magnetic anisotropy than the electrodeposited NiFe film. Moreover, the films with Hc less than 10 Oe did not show clear difference between their TEM bright images and THEED patterns.

AB - The magnetic properties and the structure of electroless-deposited NiFeB films were investigated in comparison with those of electrodeposited NiFe films. The electroless-deposited NiFeB film with 27at% Fe content had the lowest coercivity, Hc, as low as 0.5 Oe with a saturation magnetic flux density, Bs, of 1.0 T. The saturation magnetostriction, λs, and the uniaxial magnetic anisotropy, Hk, were 5.0×10-6 and 10 Oe, respectively, which were larger than those of the conventional, electrodeposited permalloy film. The permeability of as-deposited Ni70Fe27B3 film was 1000 at 1 MHz. In order to improve the permeability, the film was heated at 200 °C in a magnetic field applied in the hard-axis direction to decrease the Hk value, and the permeability became 2000 at 1 MHz. The crystal structure and grain size of NiFeB and NiFe films were investigated by XRD, THEED and TEM. Both films with low Hc had an fcc structure; the grain size of the NiFeB film was smaller than 10 nm, while that of the NiFe film was larger, approximately 20 nm. The results suggested that the electroless-deposited NiFeB film had a larger magnetic anisotropy than the electrodeposited NiFe film. Moreover, the films with Hc less than 10 Oe did not show clear difference between their TEM bright images and THEED patterns.

UR - http://www.scopus.com/inward/record.url?scp=0029410344&partnerID=8YFLogxK

UR - http://www.scopus.com/inward/citedby.url?scp=0029410344&partnerID=8YFLogxK

M3 - Article

VL - E78-C

SP - 1530

EP - 1535

JO - IEICE Transactions on Electronics

JF - IEICE Transactions on Electronics

SN - 0916-8524

IS - 11

ER -