Microstructure and oxidation behaviour of Ir-rich Ir-Al binary alloys

Z. B. Bao, H. Murakami, Y. Yamabe-Mitarai

研究成果: Article査読

13 被引用数 (Scopus)

抄録

In the current study, alloys of Ir-11Al, Ir-23Al, Ir-30Al, Ir-41Al and Ir-45Al (at.%) were prepared to investigate the microstructure and oxidation behaviour of Ir-rich Ir-Al alloys. Ir(Al)ss and/or β-IrAl intermetallic phases were found to exist in the prepared alloys. During isothermal oxidation at 1100°C, the Ir(Al)ss and β-IrAl individually changed to porous and dense Al2O3. The microstructure of the oxide scale formed on Ir-23Al was similar to that of its former alloy which possessed a dendrite-like configuration. It was found that the mass change of Ir-45Al followed a parabolic law, showing the best oxidation resistance among the Ir-Al alloys.

本文言語English
ページ(範囲)306-311
ページ数6
ジャーナルCorrosion Science
87
DOI
出版ステータスPublished - 2014 10
外部発表はい

ASJC Scopus subject areas

  • Chemistry(all)
  • Chemical Engineering(all)
  • Materials Science(all)

フィンガープリント 「Microstructure and oxidation behaviour of Ir-rich Ir-Al binary alloys」の研究トピックを掘り下げます。これらがまとまってユニークなフィンガープリントを構成します。

引用スタイル