Microstructure and role of outermost coating for tensile strength of SiC fiber

S. Q. Guo, Y. Kagawa, Y. Tanaka, C. Masuda

研究成果: Article

51 引用 (Scopus)

抜粋

The detailed microstructure of the SiC fiber surface and the outermost coating of SiC(SCS-6) fiber are observed using transmission electron microscopy (TEM) and high resolution electron microscopy (HREM). The tensile strengths of the SiC fibers: uncoated fiber (SCS-0), coated fiber (SCS-6) and extracted fiber from fatigue-loaded SiC(SCS-6) fiber-reinforced Ti-15-3 composite are determined. Fractographic analysis is done on these fibers and the mirror radius is compared with the tensile strength. Thickness of the outermost coating is ≈3.6 μm and it consists of three different layers (i.e. sublayers I, II and III). Basically, these sublayers consist of a carbon matrix in which β-SiC crystallites are dispersed. The fracture toughness of the SiC fiber is ≈3.3 MPa m1/2. The outermost coating increases the fiber strength twofold because it reduces stress concentration at the surface of the SiC fiber. The tensile strength of the extracted fiber (SCS-6) from fatigue-loaded specimens shows a reduced strength which is attributed to the debonding of the outermost coating while the composite is loaded.

元の言語English
ページ(範囲)4941-4954
ページ数14
ジャーナルActa Materialia
46
発行部数14
出版物ステータスPublished - 1998 9 1
外部発表Yes

ASJC Scopus subject areas

  • Materials Science(all)
  • Electronic, Optical and Magnetic Materials
  • Metals and Alloys

フィンガープリント Microstructure and role of outermost coating for tensile strength of SiC fiber' の研究トピックを掘り下げます。これらはともに一意のフィンガープリントを構成します。

  • これを引用

    Guo, S. Q., Kagawa, Y., Tanaka, Y., & Masuda, C. (1998). Microstructure and role of outermost coating for tensile strength of SiC fiber. Acta Materialia, 46(14), 4941-4954.