ON CORROSION FATIGUE MECHANISMS FOR S45C AND SCM435 STEELS IN ROTATING BENDING.

Chitoshi Masuda, Satoshi Nishijima, Takayuki Abe, Hideshi Sumiyoshi

研究成果: Article

抄録

Morphology of surface damage and small cracks by the corrosion fatigue was studied for quenched and tempered carbon steel S45C and Cr-Mo steel SCM435 in a deionized water and 3% NaCl water environments under rotating bending at frequencies from 0. 03 to 30 Hz. In saline water the fatigue strength of the two steels decreased monotonously with increasing number of cycles and testing time, while in the pure water a kind of temporal fatigue limit was observed for frequencies higher than 3 Hz. In the latter case fatigue crack was arrested by the closure effect of corrosion porduct for certain periods but this was diminished by dissolution after enough long test duration.

元の言語English
ページ(範囲)1019-1025
ページ数7
ジャーナルNippon Kikai Gakkai Ronbunshu, A Hen/Transactions of the Japan Society of Mechanical Engineers, Part A
50
発行部数453
出版物ステータスPublished - 1984 5

Fingerprint

Corrosion fatigue
Steel
Water
Deionized water
Saline water
Carbon steel
Dissolution
Fatigue of materials
Corrosion
Cracks
Testing
Fatigue strength
Saline Waters
Fatigue cracks

ASJC Scopus subject areas

  • Mechanical Engineering

これを引用

ON CORROSION FATIGUE MECHANISMS FOR S45C AND SCM435 STEELS IN ROTATING BENDING. / Masuda, Chitoshi; Nishijima, Satoshi; Abe, Takayuki; Sumiyoshi, Hideshi.

:: Nippon Kikai Gakkai Ronbunshu, A Hen/Transactions of the Japan Society of Mechanical Engineers, Part A, 巻 50, 番号 453, 05.1984, p. 1019-1025.

研究成果: Article

Masuda, Chitoshi ; Nishijima, Satoshi ; Abe, Takayuki ; Sumiyoshi, Hideshi. / ON CORROSION FATIGUE MECHANISMS FOR S45C AND SCM435 STEELS IN ROTATING BENDING. :: Nippon Kikai Gakkai Ronbunshu, A Hen/Transactions of the Japan Society of Mechanical Engineers, Part A. 1984 ; 巻 50, 番号 453. pp. 1019-1025.
@article{8629f7c27389453ea4f4111b75b2b9b4,
title = "ON CORROSION FATIGUE MECHANISMS FOR S45C AND SCM435 STEELS IN ROTATING BENDING.",
abstract = "Morphology of surface damage and small cracks by the corrosion fatigue was studied for quenched and tempered carbon steel S45C and Cr-Mo steel SCM435 in a deionized water and 3{\%} NaCl water environments under rotating bending at frequencies from 0. 03 to 30 Hz. In saline water the fatigue strength of the two steels decreased monotonously with increasing number of cycles and testing time, while in the pure water a kind of temporal fatigue limit was observed for frequencies higher than 3 Hz. In the latter case fatigue crack was arrested by the closure effect of corrosion porduct for certain periods but this was diminished by dissolution after enough long test duration.",
author = "Chitoshi Masuda and Satoshi Nishijima and Takayuki Abe and Hideshi Sumiyoshi",
year = "1984",
month = "5",
language = "English",
volume = "50",
pages = "1019--1025",
journal = "Nihon Kikai Gakkai Ronbunshu, A Hen/Transactions of the Japan Society of Mechanical Engineers, Part A",
issn = "0387-5008",
publisher = "Japan Society of Mechanical Engineers",
number = "453",

}

TY - JOUR

T1 - ON CORROSION FATIGUE MECHANISMS FOR S45C AND SCM435 STEELS IN ROTATING BENDING.

AU - Masuda, Chitoshi

AU - Nishijima, Satoshi

AU - Abe, Takayuki

AU - Sumiyoshi, Hideshi

PY - 1984/5

Y1 - 1984/5

N2 - Morphology of surface damage and small cracks by the corrosion fatigue was studied for quenched and tempered carbon steel S45C and Cr-Mo steel SCM435 in a deionized water and 3% NaCl water environments under rotating bending at frequencies from 0. 03 to 30 Hz. In saline water the fatigue strength of the two steels decreased monotonously with increasing number of cycles and testing time, while in the pure water a kind of temporal fatigue limit was observed for frequencies higher than 3 Hz. In the latter case fatigue crack was arrested by the closure effect of corrosion porduct for certain periods but this was diminished by dissolution after enough long test duration.

AB - Morphology of surface damage and small cracks by the corrosion fatigue was studied for quenched and tempered carbon steel S45C and Cr-Mo steel SCM435 in a deionized water and 3% NaCl water environments under rotating bending at frequencies from 0. 03 to 30 Hz. In saline water the fatigue strength of the two steels decreased monotonously with increasing number of cycles and testing time, while in the pure water a kind of temporal fatigue limit was observed for frequencies higher than 3 Hz. In the latter case fatigue crack was arrested by the closure effect of corrosion porduct for certain periods but this was diminished by dissolution after enough long test duration.

UR - http://www.scopus.com/inward/record.url?scp=0021429038&partnerID=8YFLogxK

UR - http://www.scopus.com/inward/citedby.url?scp=0021429038&partnerID=8YFLogxK

M3 - Article

AN - SCOPUS:0021429038

VL - 50

SP - 1019

EP - 1025

JO - Nihon Kikai Gakkai Ronbunshu, A Hen/Transactions of the Japan Society of Mechanical Engineers, Part A

JF - Nihon Kikai Gakkai Ronbunshu, A Hen/Transactions of the Japan Society of Mechanical Engineers, Part A

SN - 0387-5008

IS - 453

ER -