One-step synthesis of micro-/mesoporous SnO2 spheres by solvothermal method for toluene gas sensor

Angga Hermawan, Yusuke Asakura, Miki Inada, Shu Yin*

*この研究の対応する著者

研究成果: Article査読

26 被引用数 (Scopus)

抄録

A facile solvothermal synthesis in an ethanol/acetic acid mixture for the fabrication of SnO2 with a controllable hierarchical spherical size and micro-/mesoporosity is presented. SEM, TEM and N2 adsorption/desorption investigation unveiled that the obtained SnO2 spheres exhibited a particle size in the range of 0.6–1.6 μm and a pore size of about 1.4–1.9 nm depending on the volume ratio of acetic acid to ethanol in the reaction mixture, and the spheres were constructed by nanoscale particles. Due to its micro-/mesoporous structure, the SnO2 spheres exhibited large specific surface areas over 100 m2/g. When 10 vol. % of acetic acid at 200 °C for 20 h was used for the reaction, the obtained SnO2 possessed a higher specific surface area of 145 m2/g (SnO2_10). The gas sensing property of SnO2_10 without an additional noble metal co-catalyst exhibited a large toluene sensing response (Ra/Rg) of 20.2 at 400 °C, which was about 6 times higher and acceptable selectivity compared to those of other samples. The study found that the sensing performance in the SnO2 hierarchical spheres was influenced by several factors e.g. particle morphology, pore size and specific surface area rather than only a single parameter. Therefore, a precise control of those influencing parameters may lead to the optimum sensing property. These findings are important for the further development of the micro-/mesoporous metal-based oxide as an alternative successor for toluene gas sensor material.

本文言語English
ページ(範囲)15435-15444
ページ数10
ジャーナルCeramics International
45
12
DOI
出版ステータスPublished - 2019 8 15
外部発表はい

ASJC Scopus subject areas

  • 電子材料、光学材料、および磁性材料
  • セラミックおよび複合材料
  • プロセス化学およびプロセス工学
  • 表面、皮膜および薄膜
  • 材料化学

フィンガープリント

「One-step synthesis of micro-/mesoporous SnO<sub>2</sub> spheres by solvothermal method for toluene gas sensor」の研究トピックを掘り下げます。これらがまとまってユニークなフィンガープリントを構成します。

引用スタイル