Oxidation Resistance Improvement of Ni-Base Single-Crystal Superalloy Melted in a CaO Crucible

Takuya Sugiyama, Satoshi Utada, Tadaharu Yokokawa, Makoto Osawa, Kyoko Kawagishi, Shinsuke Suzuki, Hiroshi Harada

研究成果: Article査読

4 被引用数 (Scopus)

抄録

An advanced Ni-base single-crystal superalloy, TMS-238, has the highest temperature capability, but there is still potential to improve its high-temperature properties. In the present study, aiming for that further improvement, TMS-238 was melted in a CaO crucible, which replaced an Al2O3 crucible. Creep tests at 1100 °C/137 MPa and cyclic oxidation tests at 1100 °C were conducted to compare the high-temperature properties of TMS-238 melted in an Al2O3vs a CaO crucible. Regardless of the melting crucible, the creep properties of the samples were equivalent. Meanwhile, TMS-238 melted in a CaO crucible exhibited better oxidation resistance. Although the composition of the oxide scale was almost the same, the sample melted in an Al2O3 crucible had its oxide scale spalled, while a continuous oxide scale was formed on the sample melted in a CaO crucible. Dissolved Ca capturing S as CaS and preventing segregation of S at the metal-oxide interface is a possible reason for the improvement of the oxide scale adhesiveness. The results indicated that melting in a CaO crucible can improve the oxidation resistance of the original superalloys while maintaining their creep properties.

本文言語English
ページ(範囲)3903-3911
ページ数9
ジャーナルMetallurgical and Materials Transactions A: Physical Metallurgy and Materials Science
50
8
DOI
出版ステータスPublished - 2019 8 15

ASJC Scopus subject areas

  • Condensed Matter Physics
  • Mechanics of Materials
  • Metals and Alloys

フィンガープリント 「Oxidation Resistance Improvement of Ni-Base Single-Crystal Superalloy Melted in a CaO Crucible」の研究トピックを掘り下げます。これらがまとまってユニークなフィンガープリントを構成します。

引用スタイル