Phase equilibria between the B2, L12, and fcc phases in the Ir-Ni-Al system

Y. Yamabe-Mitarai, T. Aoyagi, K. Nishida, H. Aoki, T. Abe, H. Murakami

研究成果: Article

9 引用 (Scopus)

抜粋

The isotherms of the Ir-Ni-Al in the composition range up to 50 at% Al are presented at 1573 K. The phase constitution and microstructure of the Ir-Ni-Al alloys were examined using X-ray diffractometry (XRD), scanning electron microscopy (SEM) with an electron probe microanalyzer (EPMA), and transmission electron microscopy (TEM) after heat treatment at 1573 K for 168 h. The B2-NiAl and B2-IrAl phases connected with each other at 1573 K. The highest solubility limit of Ir into Ni3Al was about 3.5 at% in the tested alloys. Then, a wide fcc + B2 and a narrow fcc + L12 and B2 + L12 two-phase region appeared in the isothermal section. In part of the B2 phase, a martensitic transformation from the B2 to the L10 phase was observed.

元の言語English
ページ(範囲)479-488
ページ数10
ジャーナルIntermetallics
15
発行部数4
DOI
出版物ステータスPublished - 2007 4 1
外部発表Yes

ASJC Scopus subject areas

  • Chemistry(all)
  • Mechanics of Materials
  • Mechanical Engineering
  • Metals and Alloys
  • Materials Chemistry

フィンガープリント Phase equilibria between the B2, L1<sub>2</sub>, and fcc phases in the Ir-Ni-Al system' の研究トピックを掘り下げます。これらはともに一意のフィンガープリントを構成します。

  • これを引用