PHOSPHORUS DISTRIBUTION BETWEEN CaO-CONTAINING SLAG AND CARBON-SATURATED IRON AT HOT METAL TEMPERATURES.

Kimihisa Ito*, Nobuo Sano

*この研究の対応する著者

研究成果: Article査読

33 被引用数 (Scopus)

抄録

To decrease the impurity, such as P or S, to the lowest concentration is desired for making a high quality steel. The equilibrium distribution of phosphorus between a solid iron strip and three CaO-bearing systems measured in the temperature range from 1200 degree C to 1400 degree C. The CaO-SiO//2-FeO system has very high dephosphorizing capacity when it is saturated with 2CaO:SiO//2. The CaO-CaF//2-FeO system containing a large amount of CaO and CaF//2 has a high distribution ratio of phosphorus between slag and carbon-saturated iron. When FeO content is low, the CaO-SiO//2-CaF//2-FeO system containing a large amount of CaO has a very high phosphate capacity. In general, iron oxide tends to decrease the phosphate capacity of basic slags.

本文言語English
ページ(範囲)1747-1754
ページ数8
ジャーナルTetsu-To-Hagane/Journal of the Iron and Steel Institute of Japan
69
15
DOI
出版ステータスPublished - 1983 1 1
外部発表はい

ASJC Scopus subject areas

  • 凝縮系物理学
  • 物理化学および理論化学
  • 金属および合金
  • 材料化学

フィンガープリント

「PHOSPHORUS DISTRIBUTION BETWEEN CaO-CONTAINING SLAG AND CARBON-SATURATED IRON AT HOT METAL TEMPERATURES.」の研究トピックを掘り下げます。これらがまとまってユニークなフィンガープリントを構成します。

引用スタイル