Porous nitrogen-doped carbon nanotubes derived from tubular polypyrrole for energy-storage applications

Guiyin Xu, Bing Ding, Ping Nie, Laifa Shen, Jie Wang, Xiaogang Zhang*

*この研究の対応する著者

研究成果: Article査読

154 被引用数 (Scopus)

抄録

Porous nitrogen-doped carbon nanotubes (PNCNTs) with a high specific surface area (1765 m2 g-1) and a large pore volume (1.28 cm3 g-1) have been synthesized from a tubular polypyrrole (T-PPY). The inner diameter and wall thickness of the PNCNTs are about 55 nm and 22 nm, respectively. This material shows extremely promising properties for both supercapacitors and for encapsulating sulfur as a superior cathode material for high-performance lithium-sulfur (Li-S) batteries. At a current density of 0.5 A g-1, PNCNT presents a high specific capacitance of 210 F g -1, as well as excellent cycling stability at a current density of 2 A g-1. When the S/PNCNT composite was tested as the cathode material for Li-S batteries, the initial discharge capacity was 1341 mAh g-1 at a current rate of 1 C and, even after 50 cycles at the same rate, the high reversible capacity was retained at 933 mAh g-1. The promising electrochemical energy-storage performance of the PNCNTs can be attributed to their excellent conductivity, large surface area, nitrogen doping, and unique pore-size distribution. Rich man, pore man: Porous nitrogen-doped carbon nanotubes (PNCNT) that are derived from a tubular polypyrrole (T-PPY) exhibit great potential for both electrical double-layer supercapacitors and lithium-sulfur batteries (see scheme).

本文言語English
ページ(範囲)12306-12312
ページ数7
ジャーナルChemistry - A European Journal
19
37
DOI
出版ステータスPublished - 2013 9月 9
外部発表はい

ASJC Scopus subject areas

  • 触媒
  • 有機化学

フィンガープリント

「Porous nitrogen-doped carbon nanotubes derived from tubular polypyrrole for energy-storage applications」の研究トピックを掘り下げます。これらがまとまってユニークなフィンガープリントを構成します。

引用スタイル