β-Ga2O3 is gaining increasing attention from power device engineers owing to its wide bandgap and fabrication potential of low-cost, large-diameter substrates. Atomic-layer-deposited (ALD) Al2O3 has application potential for the gate insulation and surface passivation of β-Ga2O3 devices, which cannot incorporate a well-established SiO2/Si system. To improve the device performance and reliability, the effect of postdeposition annealing (PDA) on the gate insulation characteristics of Al/ALD-Al2O3/(001) β-Ga2O3 capacitors was comprehensively investigated. As in previous studies, PDA at 700 °C and higher sharply reduced the capacitor leakage current by three orders of magnitude. This threshold temperature was 100 °C lower than that for GaN devices. Space-charge-controlled field emission analysis revealed that the current reduction was achieved via conduction-band-offset enhancement from 1.45 to 2.2 eV. These changes were caused by Al2O3 crystallization, which started at 650 °C according to an x-ray diffraction analysis. Selective-area electron diffraction (SAED) patterns showed that the crystallized films comprised twinned γ-Al2O3, wherein the (111) planes are parallel to the sawtooth β-Ga2O3 (101) planes with epitaxial relations of γ-Al2O3 [0 1 ¯ 1] || β-Ga2O3  and γ-Al2O3 [01 1 ¯] || β-Ga2O3 . This epitaxy was realized by three-dimensional oxygen sublattice matching with relatively small misfits of less than 1%, 1%, and 8% along the γ-Al2O3 [2 1 ¯ 1 ¯], , and [01 1 ¯] directions, respectively. Furthermore, the SAED patterns displayed diffraction spots specific to triaxially tripled γ-Al2O3. This is yet to be identified as δ-Al2O3. Contrary to expectations, PDA magnified the bias instability of β-Ga2O3 capacitors, supposedly owing to the Al2O3 and Ga2O3 solid-solution reaction, which contrasts with the previous significant improvement in GaN capacitors. However, PDA negligibly affected the β-Ga2O3 capacitor interface characteristics. This result also contrasts sharply with the previous results obtained for GaN capacitors that experienced a PDA-induced increase in both interface states and flat-band voltage. This apparent thermal stability of Al2O3/(001) β-Ga2O3 interface can be ascribed to the aforementioned small lattice misfit at the γ-Al2O3/(101) β-Ga2O3 interface, which contrasts with the 12% misfit at the γ-Al2O3/(0001) GaN interface. These findings form the foundation for developing technologies to enhance the performance and reliability of ALD-Al2O3/β-Ga2O3 devices. Specifically, based on them, a guideline for reducing the bias instability is proposed.
|ジャーナル||Journal of Vacuum Science and Technology B: Nanotechnology and Microelectronics|
|出版ステータス||Published - 2021 12 1|
ASJC Scopus subject areas