Prediction of residual stress in grey cast iron: Experiment and analysis

Yuichi Motoyama, Hiroki Takahashi, Toshimitsu Okane, Yoya Fukuda, Makoto Yoshida

研究成果: Conference contribution

抜粋

This study showed that the thermal stress analysis for the stress lattice casting should use the element that is able to represent the bending deformation in principle for bending of the thin parts of the stress lattice. The thermal stress analysis successfully predicted the residual stress of the stress lattice due to the temperature difference between the thick and thin part with 11% difference using the second order tetrahedral element. However, the result of the simulation indicated that the magnitude of the residual stress due to the temperature difference in the cross section of the thick part was the same as that attributed to temperature difference between the thick and thin parts. This result indicated that the verification of the prediction accuracy of its residual stress must be conducted before applying the FEM to the prediction of the industrial casting residual stress.

元の言語English
ホスト出版物のタイトルMaterials Science and Technology Conference and Exhibition 2013, MS and T 2013
ページ885-892
ページ数8
出版物ステータスPublished - 2013 12 1
イベントMaterials Science and Technology Conference and Exhibition 2013, MS and T 2013 - Montreal, QC, Canada
継続期間: 2013 10 272013 10 31

出版物シリーズ

名前Materials Science and Technology Conference and Exhibition 2013, MS and T 2013
2

Conference

ConferenceMaterials Science and Technology Conference and Exhibition 2013, MS and T 2013
Canada
Montreal, QC
期間13/10/2713/10/31

ASJC Scopus subject areas

  • Mechanics of Materials

フィンガープリント Prediction of residual stress in grey cast iron: Experiment and analysis' の研究トピックを掘り下げます。これらはともに一意のフィンガープリントを構成します。

  • これを引用

    Motoyama, Y., Takahashi, H., Okane, T., Fukuda, Y., & Yoshida, M. (2013). Prediction of residual stress in grey cast iron: Experiment and analysis. : Materials Science and Technology Conference and Exhibition 2013, MS and T 2013 (pp. 885-892). (Materials Science and Technology Conference and Exhibition 2013, MS and T 2013; 巻数 2).