Preparation, characterization, and surface modification of periodic mesoporous silicon-aluminum-carbon-nitrogen frameworks

O. Majoulet, C. Salameh, M. E. Schuster, U. B. Demirci, Y. Sugahara, S. Bernard*, P. Miele

*この研究の対応する著者

研究成果: Article査読

35 被引用数 (Scopus)

抄録

Periodic mesoporous silicon-aluminum-carbon-nitrogen (Si/Al/C/N) frameworks with P6mm hexagonal symmetry were synthesized by a solvent nanocasting route using mesoporous carbon (CMK-3) as hard template and preceramic polymers containing both -[R1R2Si-N(R3)]n- and -[R4Al-N(R5)]n- backbones (with R 1 = R2 = R3 = R4 = H and R 5 = CH2CH3) as ceramic precursors. The preceramic polymers are prepared through a simple and cost-effective procedure by blending poly(perhydropolysilazane) and poly(ethyliminoalane) as precursors of silicon nitride/silicon (Si3N4/Si) and carbon-containing aluminum nitride (Al/C/N), respectively. The blended polymers with various and controlled Al:Si ratios were infiltrated into the porous structure of CMK-3, followed by a pyrolysis-template removal cycle performed under nitrogen at 1000 C (2 h, ceramic conversion), then in an ammonia atmosphere at 1000 C (5 h, template removal). This procedure resulted in the formation of periodic mesoporous Si/Al/C/N frameworks with surface areas of 182-326 m2 g-1, a pore size distribution of 4.1-5.9 nm, and pore volumes in the range of 0.51-0.65 cm3 g-1. The uniformity of the mesopores and periodicity of the obtained amorphous micrometer-size powders, studied by transmission electron microscopy (TEM), small-angle X-ray diffraction (SA-XRD), and N2 sorption, are affected by the Al:Si ratio. Amorphous materials did not exhibit weight change up to 1400-1470 C in flowing nitrogen, and their behavior in air, up to 1000 C (with dwelling time of 5 h), is dependent on the proportion of AlN and Si 3N4 phases. The as-obtained powders then were decorated with Pt (nano)particles by impregnation to form supported catalysts. The as-formed catalysts showed attractive reactivity and robustness in our probe reaction, namely, the hydrolysis of an alkaline solution of sodium borohydride at 80 C. Our main results are reported therein.

本文言語English
ページ(範囲)3957-3970
ページ数14
ジャーナルChemistry of Materials
25
20
DOI
出版ステータスPublished - 2013 10月 22

ASJC Scopus subject areas

  • 化学 (全般)
  • 化学工学(全般)
  • 材料化学

フィンガープリント

「Preparation, characterization, and surface modification of periodic mesoporous silicon-aluminum-carbon-nitrogen frameworks」の研究トピックを掘り下げます。これらがまとまってユニークなフィンガープリントを構成します。

引用スタイル