Preparation of segmented, high molecular weight, aliphatic poly(ether-urea) copolymers in isopropanol. In-situ FTIR studies and polymer synthesis

Iskender Yilgor*, Brian D. Mather, Serkan Unal, Emel Yilgor, Timothy Edward Long

*この研究の対応する著者

研究成果: Article査読

47 被引用数 (Scopus)

抄録

The use of isopropanol (IPA) as the reaction solvent for the preparation of high molecular weight segmented polyether-urea copolymers based on cycloaliphatic diisocyanates was investigated. Reactivity of IPA with bis(4-isocyanatohexyl)methane (HMDI) and isophorone diisocyanate (IPDI) was studied between 0 and 40°C using in-situ FTIR spectroscopy. HMDI, which has secondary isocyanate groups, shows a very slow reaction with a large excess of IPA at 0 and 23°C. Analysis of the kinetic data indicates an activation energy of 51 kJ/mol for the reaction between HMDI and IPA. As expected, IPDI, which has both a primary and a secondary isocyanate (NCO) group, reacts faster with IPA compared with HMDI, which only has secondary NCO groups. However, the rate of reaction of IPDI with IPA at 0°C is extremely slow (approximately 1% consumption of isocyanate in 60 min) thus allowing the use of IPA as the reaction solvent for polyether-urea synthesis. Preparation of high molecular weight, high-strength HMDI and IPDI based polyether-urea segmented copolymers in IPA has been demonstrated. Thermal analysis and stress-strain analyses were used to characterize the products.

本文言語English
ページ(範囲)5829-5836
ページ数8
ジャーナルPolymer
45
17
DOI
出版ステータスPublished - 2004 8月 5
外部発表はい

ASJC Scopus subject areas

  • ポリマーおよびプラスチック
  • 有機化学

フィンガープリント

「Preparation of segmented, high molecular weight, aliphatic poly(ether-urea) copolymers in isopropanol. In-situ FTIR studies and polymer synthesis」の研究トピックを掘り下げます。これらがまとまってユニークなフィンガープリントを構成します。

引用スタイル