Preparation of Transparent Bulk TiO2/PMMA Hybrids with Improved Refractive Indices via an in Situ Polymerization Process Using TiO2 Nanoparticles Bearing PMMA Chains Grown by Surface-Initiated Atom Transfer Radical Polymerization

Satoshi Maeda, Masato Fujita, Naokazu Idota, Kimihiro Matsukawa, Yoshiyuki Sugahara

    研究成果: Article

    8 引用 (Scopus)

    抄録

    Transparent TiO2/PMMA hybrids with a thickness of 5 mm and improved refractive indices were prepared by in situ polymerization of methyl methacrylate (MMA) in the presence of TiO2 nanoparticles bearing poly(methyl methacrylate) (PMMA) chains grown using surface-initiated atom transfer radical polymerization (SI-ATRP), and the effect of the chain length of modified PMMA on the dispersibility of modified TiO2 nanoparticles in the bulk hybrids was investigated. The surfaces of TiO2 nanoparticles were modified with both m-(chloromethyl)phenylmethanoyloxymethylphosphonic acid bearing a terminal ATRP initiator and isodecyl phosphate with a high affinity for common organic solvents, leading to sufficient dispersibility of the surface-modified particles in toluene. Subsequently, SI-ATRP of MMA was achieved from the modified surfaces of the TiO2 nanoparticles without aggregation of the nanoparticles in toluene. The molecular weights of the PMMA chains cleaved from the modified TiO2 nanoparticles increased with increases in the prolonging of the polymerization period, and these exhibited a narrow distribution, indicating chain growth controlled by SI-ATRP. The nanoparticles bearing PMMA chains were well-dispersed in MMA regardless of the polymerization period. Bulk PMMA hybrids containing modified TiO2 nanoparticles with a thickness of 5 mm were prepared by in situ polymerization of the MMA dispersion. The transparency of the hybrids depended significantly on the chain length of the modified PMMA on the nanoparticles, because the modified PMMA of low molecular weight induced aggregation of the TiO2 nanoparticles during the in situ polymerization process. The refractive indices of the bulk hybrids could be controlled by adjusting the TiO2 content and could be increased up to 1.566 for 6.3 vol % TiO2 content (1.492 for pristine PMMA).

    元の言語English
    ページ(範囲)34762-34769
    ページ数8
    ジャーナルACS Applied Materials and Interfaces
    8
    発行部数50
    DOI
    出版物ステータスPublished - 2016 12 21

    Fingerprint

    Bearings (structural)
    Atom transfer radical polymerization
    Polymethyl Methacrylate
    Polymethyl methacrylates
    Refractive index
    Polymerization
    Nanoparticles
    Methacrylates
    Toluene
    Chain length
    Agglomeration
    Molecular weight
    Transparency
    Organic solvents
    Phosphates

    ASJC Scopus subject areas

    • Materials Science(all)

    これを引用

    @article{29df4e98ae824d3fab30cad21c820a88,
    title = "Preparation of Transparent Bulk TiO2/PMMA Hybrids with Improved Refractive Indices via an in Situ Polymerization Process Using TiO2 Nanoparticles Bearing PMMA Chains Grown by Surface-Initiated Atom Transfer Radical Polymerization",
    abstract = "Transparent TiO2/PMMA hybrids with a thickness of 5 mm and improved refractive indices were prepared by in situ polymerization of methyl methacrylate (MMA) in the presence of TiO2 nanoparticles bearing poly(methyl methacrylate) (PMMA) chains grown using surface-initiated atom transfer radical polymerization (SI-ATRP), and the effect of the chain length of modified PMMA on the dispersibility of modified TiO2 nanoparticles in the bulk hybrids was investigated. The surfaces of TiO2 nanoparticles were modified with both m-(chloromethyl)phenylmethanoyloxymethylphosphonic acid bearing a terminal ATRP initiator and isodecyl phosphate with a high affinity for common organic solvents, leading to sufficient dispersibility of the surface-modified particles in toluene. Subsequently, SI-ATRP of MMA was achieved from the modified surfaces of the TiO2 nanoparticles without aggregation of the nanoparticles in toluene. The molecular weights of the PMMA chains cleaved from the modified TiO2 nanoparticles increased with increases in the prolonging of the polymerization period, and these exhibited a narrow distribution, indicating chain growth controlled by SI-ATRP. The nanoparticles bearing PMMA chains were well-dispersed in MMA regardless of the polymerization period. Bulk PMMA hybrids containing modified TiO2 nanoparticles with a thickness of 5 mm were prepared by in situ polymerization of the MMA dispersion. The transparency of the hybrids depended significantly on the chain length of the modified PMMA on the nanoparticles, because the modified PMMA of low molecular weight induced aggregation of the TiO2 nanoparticles during the in situ polymerization process. The refractive indices of the bulk hybrids could be controlled by adjusting the TiO2 content and could be increased up to 1.566 for 6.3 vol {\%} TiO2 content (1.492 for pristine PMMA).",
    keywords = "dispersibility, surface-initiated atom transfer radical polymerization, TiO/PMMA hybrids, transparency",
    author = "Satoshi Maeda and Masato Fujita and Naokazu Idota and Kimihiro Matsukawa and Yoshiyuki Sugahara",
    year = "2016",
    month = "12",
    day = "21",
    doi = "10.1021/acsami.6b10427",
    language = "English",
    volume = "8",
    pages = "34762--34769",
    journal = "ACS applied materials & interfaces",
    issn = "1944-8244",
    publisher = "American Chemical Society",
    number = "50",

    }

    TY - JOUR

    T1 - Preparation of Transparent Bulk TiO2/PMMA Hybrids with Improved Refractive Indices via an in Situ Polymerization Process Using TiO2 Nanoparticles Bearing PMMA Chains Grown by Surface-Initiated Atom Transfer Radical Polymerization

    AU - Maeda, Satoshi

    AU - Fujita, Masato

    AU - Idota, Naokazu

    AU - Matsukawa, Kimihiro

    AU - Sugahara, Yoshiyuki

    PY - 2016/12/21

    Y1 - 2016/12/21

    N2 - Transparent TiO2/PMMA hybrids with a thickness of 5 mm and improved refractive indices were prepared by in situ polymerization of methyl methacrylate (MMA) in the presence of TiO2 nanoparticles bearing poly(methyl methacrylate) (PMMA) chains grown using surface-initiated atom transfer radical polymerization (SI-ATRP), and the effect of the chain length of modified PMMA on the dispersibility of modified TiO2 nanoparticles in the bulk hybrids was investigated. The surfaces of TiO2 nanoparticles were modified with both m-(chloromethyl)phenylmethanoyloxymethylphosphonic acid bearing a terminal ATRP initiator and isodecyl phosphate with a high affinity for common organic solvents, leading to sufficient dispersibility of the surface-modified particles in toluene. Subsequently, SI-ATRP of MMA was achieved from the modified surfaces of the TiO2 nanoparticles without aggregation of the nanoparticles in toluene. The molecular weights of the PMMA chains cleaved from the modified TiO2 nanoparticles increased with increases in the prolonging of the polymerization period, and these exhibited a narrow distribution, indicating chain growth controlled by SI-ATRP. The nanoparticles bearing PMMA chains were well-dispersed in MMA regardless of the polymerization period. Bulk PMMA hybrids containing modified TiO2 nanoparticles with a thickness of 5 mm were prepared by in situ polymerization of the MMA dispersion. The transparency of the hybrids depended significantly on the chain length of the modified PMMA on the nanoparticles, because the modified PMMA of low molecular weight induced aggregation of the TiO2 nanoparticles during the in situ polymerization process. The refractive indices of the bulk hybrids could be controlled by adjusting the TiO2 content and could be increased up to 1.566 for 6.3 vol % TiO2 content (1.492 for pristine PMMA).

    AB - Transparent TiO2/PMMA hybrids with a thickness of 5 mm and improved refractive indices were prepared by in situ polymerization of methyl methacrylate (MMA) in the presence of TiO2 nanoparticles bearing poly(methyl methacrylate) (PMMA) chains grown using surface-initiated atom transfer radical polymerization (SI-ATRP), and the effect of the chain length of modified PMMA on the dispersibility of modified TiO2 nanoparticles in the bulk hybrids was investigated. The surfaces of TiO2 nanoparticles were modified with both m-(chloromethyl)phenylmethanoyloxymethylphosphonic acid bearing a terminal ATRP initiator and isodecyl phosphate with a high affinity for common organic solvents, leading to sufficient dispersibility of the surface-modified particles in toluene. Subsequently, SI-ATRP of MMA was achieved from the modified surfaces of the TiO2 nanoparticles without aggregation of the nanoparticles in toluene. The molecular weights of the PMMA chains cleaved from the modified TiO2 nanoparticles increased with increases in the prolonging of the polymerization period, and these exhibited a narrow distribution, indicating chain growth controlled by SI-ATRP. The nanoparticles bearing PMMA chains were well-dispersed in MMA regardless of the polymerization period. Bulk PMMA hybrids containing modified TiO2 nanoparticles with a thickness of 5 mm were prepared by in situ polymerization of the MMA dispersion. The transparency of the hybrids depended significantly on the chain length of the modified PMMA on the nanoparticles, because the modified PMMA of low molecular weight induced aggregation of the TiO2 nanoparticles during the in situ polymerization process. The refractive indices of the bulk hybrids could be controlled by adjusting the TiO2 content and could be increased up to 1.566 for 6.3 vol % TiO2 content (1.492 for pristine PMMA).

    KW - dispersibility

    KW - surface-initiated atom transfer radical polymerization

    KW - TiO/PMMA hybrids

    KW - transparency

    UR - http://www.scopus.com/inward/record.url?scp=85006932902&partnerID=8YFLogxK

    UR - http://www.scopus.com/inward/citedby.url?scp=85006932902&partnerID=8YFLogxK

    U2 - 10.1021/acsami.6b10427

    DO - 10.1021/acsami.6b10427

    M3 - Article

    AN - SCOPUS:85006932902

    VL - 8

    SP - 34762

    EP - 34769

    JO - ACS applied materials & interfaces

    JF - ACS applied materials & interfaces

    SN - 1944-8244

    IS - 50

    ER -