Quaternary ammonium-biphosphate ion-pair based copolymers with continuous H+ transport channels for high-temperature proton exchange membrane

Junqiao Jiang, Zhen Li, Min Xiao, Shuanjin Wang, Kenji Miyatake, Yuezhong Meng*

*この研究の対応する著者

研究成果: Article査読

1 被引用数 (Scopus)

抄録

Phosphoric acid (PA)-doped polymer electrolyte membranes are the most promising materials for high-temperature proton exchange membranes (HT-PEMs). However, their development is subject to the compromise between proton conductivity and phosphoric acid (PA) doping level. Here, an ether-free QPAF-4 membrane (a copolymer containing perfluoroalkylene and fluorenyl groups with pendant ammonium groups) is directly doped with phosphoric acid and studied as HT-PEMs. Due to the intrinsic micro-phase separation structure of QPAF-4 matrix and strong interaction of quaternary ammonium (QA)-PA, the PA-doped membranes possess high proton conductivity and eminent PA retention at comparatively low PA doping level, respectively. The QPAF-4 membrane with 150% PA uptake (QPAF-4-150%PA) offers a proton conductivity of 52 mS cm−1 at 160 °C. As expected, the single cell with QPAF-4-150%PA membrane shows the maximum peak power density of 683 mW cm−2 at 160 °C under anhydrous condition. Meanwhile, the single cell exhibits excellent durability over a period of 60 h with only a slight reduction in voltage of 3.1%. These results indicate that the as-prepared PA-doped quaternized polymer with micro-phase separation structure seems to offer a promising way to develop performing and long-life HT-PEMs with low PA doping levels.

本文言語English
論文番号120878
ジャーナルJournal of Membrane Science
660
DOI
出版ステータスPublished - 2022 10月 15

ASJC Scopus subject areas

  • 生化学
  • 材料科学(全般)
  • 物理化学および理論化学
  • ろ過および分離

フィンガープリント

「Quaternary ammonium-biphosphate ion-pair based copolymers with continuous H+ transport channels for high-temperature proton exchange membrane」の研究トピックを掘り下げます。これらがまとまってユニークなフィンガープリントを構成します。

引用スタイル