抄録
The amphiphilic diblock copolymer of poly(ethylene oxide) (PEO) and poly(methacrylate) bearing azobenzene liquid crystalline units (PMA(Az)) gave a well-aligned cylindrical nanostructure, in which both PEO and PMA domains were bicontinuous throughout the film thickness. A point-functionalized block copolymer with photo- and electrochemically active perylenediimide PEO 114-Jb-pery-Jb-PMA(Az)n was synthesized by atom transfer radical polymerization with narrow polydispersity of 1.15. The spin-cast film from chloroform solution gave a hexagonally aligned but mono-directionally distorted cylindrical nanostructure throughout the film thickness. The fact that the relative intensity of the fluorescence at 638 nm, which is assigned as dimer emission of perylenediimide, was enhanced upon annealing implies that the strongly n-n stacked structure of perylenediimide was formed at the interface of PEO and PMA domains during the formation of aligned nanostructure.
元の言語 | English |
---|---|
ホスト出版物のタイトル | Polymer Preprints, Japan |
ページ | 4665-4666 |
ページ数 | 2 |
巻 | 55 |
エディション | 2 |
出版物ステータス | Published - 2006 |
外部発表 | Yes |
イベント | 55th Society of Polymer Science Japan Symposium on Macromolecules - Toyama 継続期間: 2006 9 20 → 2006 9 22 |
Other
Other | 55th Society of Polymer Science Japan Symposium on Macromolecules |
---|---|
市 | Toyama |
期間 | 06/9/20 → 06/9/22 |
Fingerprint
ASJC Scopus subject areas
- Engineering(all)
これを引用
Regiospecific accumulation of photofunctional units at microphase segregation interface of amphiphilic diblock copolymer. / Asaoka, Sadayuki; Miyatani, Tomohisa; Komura, Motonori; Iyoda, Tomokazu; Nishikitani, Yoshinori; Kubo, Takaya; Uchida, Souichi.
Polymer Preprints, Japan. 巻 55 2. 編 2006. p. 4665-4666.研究成果: Conference contribution
}
TY - GEN
T1 - Regiospecific accumulation of photofunctional units at microphase segregation interface of amphiphilic diblock copolymer
AU - Asaoka, Sadayuki
AU - Miyatani, Tomohisa
AU - Komura, Motonori
AU - Iyoda, Tomokazu
AU - Nishikitani, Yoshinori
AU - Kubo, Takaya
AU - Uchida, Souichi
PY - 2006
Y1 - 2006
N2 - The amphiphilic diblock copolymer of poly(ethylene oxide) (PEO) and poly(methacrylate) bearing azobenzene liquid crystalline units (PMA(Az)) gave a well-aligned cylindrical nanostructure, in which both PEO and PMA domains were bicontinuous throughout the film thickness. A point-functionalized block copolymer with photo- and electrochemically active perylenediimide PEO 114-Jb-pery-Jb-PMA(Az)n was synthesized by atom transfer radical polymerization with narrow polydispersity of 1.15. The spin-cast film from chloroform solution gave a hexagonally aligned but mono-directionally distorted cylindrical nanostructure throughout the film thickness. The fact that the relative intensity of the fluorescence at 638 nm, which is assigned as dimer emission of perylenediimide, was enhanced upon annealing implies that the strongly n-n stacked structure of perylenediimide was formed at the interface of PEO and PMA domains during the formation of aligned nanostructure.
AB - The amphiphilic diblock copolymer of poly(ethylene oxide) (PEO) and poly(methacrylate) bearing azobenzene liquid crystalline units (PMA(Az)) gave a well-aligned cylindrical nanostructure, in which both PEO and PMA domains were bicontinuous throughout the film thickness. A point-functionalized block copolymer with photo- and electrochemically active perylenediimide PEO 114-Jb-pery-Jb-PMA(Az)n was synthesized by atom transfer radical polymerization with narrow polydispersity of 1.15. The spin-cast film from chloroform solution gave a hexagonally aligned but mono-directionally distorted cylindrical nanostructure throughout the film thickness. The fact that the relative intensity of the fluorescence at 638 nm, which is assigned as dimer emission of perylenediimide, was enhanced upon annealing implies that the strongly n-n stacked structure of perylenediimide was formed at the interface of PEO and PMA domains during the formation of aligned nanostructure.
KW - Atom transfer radical polymerization
KW - Microphase segregation interface
KW - Regiospecific functionalization
UR - http://www.scopus.com/inward/record.url?scp=33846122686&partnerID=8YFLogxK
UR - http://www.scopus.com/inward/citedby.url?scp=33846122686&partnerID=8YFLogxK
M3 - Conference contribution
AN - SCOPUS:33846122686
VL - 55
SP - 4665
EP - 4666
BT - Polymer Preprints, Japan
ER -