Roll casting of aluminum alloy strip by melt drag twin roll caster

Toshio Haga*, Shinsuke Suzuki

*この研究の対応する著者

研究成果査読

17 被引用数 (Scopus)

抄録

The present paper describes the melt drag twin roll caster, a recently devised type of high-speed and semi-solid twin roll caster which requires no lubricant to prevent the strip-sticking to the rolls. The copper rolls and extremely small separating force (0.01-0.1MPa) of the melt drag twin roll caster eliminates the tendency for the strip to adhere to the rolls, thus eliminating the need for a lubricant. Use of copper rolls and no use of the lubricant are significant factors in high-speed roll casting, and A5182 can be cast at the speeds up to 60m/min. The microstructure of the A5182 strips cast by the melt drag twin roll caster is not columnar structure but equiaxed structure. The higher the roll speed, the smaller the microstructure. The strip thickness is at the range about from 2 to 3mm.

本文言語English
ページ(範囲)165-168
ページ数4
ジャーナルJournal of Materials Processing Technology
118
1-3
DOI
出版ステータスPublished - 2001 12 3
外部発表はい

ASJC Scopus subject areas

  • セラミックおよび複合材料
  • コンピュータ サイエンスの応用
  • 金属および合金
  • 産業および生産工学

フィンガープリント

「Roll casting of aluminum alloy strip by melt drag twin roll caster」の研究トピックを掘り下げます。これらがまとまってユニークなフィンガープリントを構成します。

引用スタイル