Strontium-doped Lanthanum Manganese Oxides Studied by XPS

T. Saitoh, A. E. Bocquet, T. Mizokawa, H. Namatame, A. Fujimori, Y. Takeda, M. Takano

研究成果: Article査読

1 被引用数 (Scopus)

抄録

La1−xSrxMnO3 is a perovskite-type magnetic material. LaMnO3 and SrMnO3 are antiferromagnetic insulators while the system becomes a ferromagnetic metal in a certain Sr concentration. In ∼0.2<x<∼0.5, it shows a so-called colossal magnetoresistance (CMR) which is a phenomenon of a huge resistivity drop when a magnetic field is applied. This property has a potential application to the magnetic storage industry. The aim of this research was to understand the electronic structure of this system using photoemission spectroscopy and to elucidate the origin of the CMR phenomenon. The samples were polycrystalline and were prepared by solid-state reaction. XPS measurements were carried out using a Mg Kα source at liquid nitrogen temperature (∼80 K). In order to obtain a fresh, clean surface, the samples were scraped with a diamond file in situ, and surface aging was monitored by observing the intensity of a tail at the higher binding-energy side of the O 1s peak. The surface typically lasted for 1-2 h.

本文言語English
ページ(範囲)292-301
ページ数10
ジャーナルSurface Science Spectra
6
4
DOI
出版ステータスPublished - 1999 10 1

ASJC Scopus subject areas

  • 凝縮系物理学
  • 表面および界面
  • 表面、皮膜および薄膜

フィンガープリント

「Strontium-doped Lanthanum Manganese Oxides Studied by XPS」の研究トピックを掘り下げます。これらがまとまってユニークなフィンガープリントを構成します。

引用スタイル