Study on the capacity fading of pristine and FePO4 coated LiNi1/3Co1/3Mn1/3O2 by Electrochemical and Magnetical techniques

Xizheng Liu, De Li, Huiqiao Li, Akira Iyo, Nobuko Hanada, Masayoshi Ishida, Haoshen Zhou

研究成果: Article査読

7 被引用数 (Scopus)

抄録

Capacity fading mechanism of pristine and FePO4-coated LiNi1/3Co1/3Mn1/3O2 has been studied by electrochemical and magnetic methods. Along with cycles, significant increase of cell polarization and charger transfer resistance (Rct), which mainly cause the capacity fading at the initial charge/discharge cycles, have been observed according to the cyclic voltammetry (CV) and electrochemical impedance spectroscopy (EIS) analysis. In comparison, the existence of FePO4 coating layer can effectively suppress the deterioration of surface polarization and increase of Rct at the interface of electrode/electrolyte. The coated sample suppress the decrease of Li+ diffusion coefficient with prolonged cycles according to the galvanostatic intermittent titration technique (GITT) tests. It also shows larger Weiss constants (fitting above 130 K) and lower blocking temperatures, which indicate the surface coating can suppress the deterioration of Li/Ni disorder upon repeated cycles. This study may give the researchers some light on understanding the capacity fading mechanism of LiNi1/3Co1/3Mn1/3O2 and the effects of surface coating layer, and thus, give help to the future designing of superior coating layers for layered cathode materials in Li-ion batteries.

本文言語English
ページ(範囲)26-32
ページ数7
ジャーナルElectrochimica Acta
148
DOI
出版ステータスPublished - 2014 12 1

ASJC Scopus subject areas

  • Chemical Engineering(all)
  • Electrochemistry

フィンガープリント 「Study on the capacity fading of pristine and FePO<sub>4</sub> coated LiNi<sub>1/3</sub>Co<sub>1/3</sub>Mn<sub>1/3</sub>O<sub>2</sub> by Electrochemical and Magnetical techniques」の研究トピックを掘り下げます。これらがまとまってユニークなフィンガープリントを構成します。

引用スタイル