Superplastic forging of ZrTiCuNiBe-bulk glass for shaping of microparts

Th Zumkley, S. Suzuki, M. Seidel, S. Mechler, M. P. Macht

研究成果: Conference article査読

13 被引用数 (Scopus)

抄録

Metallic bulk glasses are suitable for near net shaping of machine parts by die-forging under small loads in the low viscous state above the glass transition temperature. However, this application is limited by phase transitions in the metastable glasses, which affect the ability of superplastic moulding by degradation of the viscous properties of the material. The thermal stability and the superplastic behavior of Zr46.8Ti8.2Cu7.5Ni10 Be27.5 bulk glass was investigated by differential scanning calorimetry, X-ray diffraction, microhardness measurements and by thermal mechanical analysis. From these measurements the temperature-time range was determined in which the glass can be forged without altering the microstructure significantly. At 643 K and 653 K, the glass remains sufficiently stable for 5 h and 3 h, respectively and the deformation is controlled by Newtonian flow. By pressing the glass with 5 MPa at 653 K a deformation of ε≈5 was attained. Microparts of 200 μm in width and up to 500 μm in height were moulded with excellent precision at 653 K and 653 K in a small load, high temperature vacuum press.

本文言語English
ページ(範囲)541-546
ページ数6
ジャーナルMaterials Science Forum
386-388
DOI
出版ステータスPublished - 2002
外部発表はい
イベントProceedings of the International Symposium on Metastable, Mechanically Alloyed and Noncrystalline Materials (ISMANAM) - Ann Arbor, MI, United States
継続期間: 2001 6 242001 6 29

ASJC Scopus subject areas

  • Materials Science(all)
  • Condensed Matter Physics
  • Mechanics of Materials
  • Mechanical Engineering

フィンガープリント 「Superplastic forging of ZrTiCuNiBe-bulk glass for shaping of microparts」の研究トピックを掘り下げます。これらがまとまってユニークなフィンガープリントを構成します。

引用スタイル