Synthesis of Al-containing mesoporous silica (KSW-2) with semi-squared channels by incorporation of Al into the framework of kanemite

Tetsuro Shigeno, Koji Inoue, Tatsuo Kimura, Naonobu Katada, Miki Niwa, Kazuyuki Kuroda*

*この研究の対応する著者

研究成果査読

17 被引用数 (Scopus)

抄録

Incorporation of Al into the framework of single-layered silicate kanemite and the formation of Al-containing mesoporous silica (Al-KSW-2) with semi-squared one-dimensional channels were surveyed. Al-containing δ-Na2Si2O5 was successfully obtained by thermal treatment of an aqueous sodium silicate solution (Na2O/SiO2 = 1:2) containing NaAlO2 up to 785-810 °C, depending on the amount of NaAlO2 added. After Al-containing δ-Na2Si2O5 was dispersed in distilled water, Al-containing kanemite (Al-kanemite) was obtained with tetrahedrally coordinated A1. The reaction of Al-kanemite with an aqueous solution of hexadecyltrimethylammonium (C16TMA) surfactant yielded a layered C16TMA-Al-kanemite complex which was converted to a mesostructured precursor of Al-KSW-2 by mild acid treatment. Tetrahedral coordination of Al was retained in the framework of Al-KSW-2 with high surface area (830 m2 g-1) and uniform semi-squared mesopores (2.7 nm), which increased the adsorption ability for cationic dye molecules.

本文言語English
ページ(範囲)883-887
ページ数5
ジャーナルJournal of Materials Chemistry
13
4
DOI
出版ステータスPublished - 2003 4 1

ASJC Scopus subject areas

  • 化学 (全般)
  • 材料化学

フィンガープリント

「Synthesis of Al-containing mesoporous silica (KSW-2) with semi-squared channels by incorporation of Al into the framework of kanemite」の研究トピックを掘り下げます。これらがまとまってユニークなフィンガープリントを構成します。

引用スタイル