Synthesis of A1-xA′xNbO3 (A = Na+, K+; A′ = La3+, Sr2+) and its electrical properties

W. Sugimoto*, T. Tahara, Y. Sugahara, K. Kuroda

*この研究の対応する著者

研究成果: Conference article査読

1 被引用数 (Scopus)

抄録

Polycrystalline samples of A1-xA′xNbO3 (A = Na+, K+; A′ = La3+, Sr2+) were prepared by solid-state reactions and the relationship between the structure and electrical properties was examined. Single-phase products were obtained for Na1-xLaxNbO3 (x≤0.1), K1-xLaxNbO3 (x≤0.15), Na1-xSrxNbO3 (x≤0.3), and K1-xSrxNbO3 (x≤0.5). The structures of the sodium-containing compounds and potassium-containing compounds were indexed according to a pseudocubic and cubic symmetry, respectively. The resistivity measurements showed semiconductive behavior for the lanthanum-containing samples. The strontium-containing samples showed semiconducting properties for x≤0.2, while a transition to metallic conduction at low temperature was observed for x>0.2.

本文言語English
ページ(範囲)361-366
ページ数6
ジャーナルMaterials Research Society Symposium - Proceedings
453
出版ステータスPublished - 1997 1 1
イベントProceedings of the 1996 MRS Fall Symposium - Boston, MA, USA
継続期間: 1996 12 21996 12 5

ASJC Scopus subject areas

  • 材料科学(全般)
  • 凝縮系物理学
  • 材料力学
  • 機械工学

フィンガープリント

「Synthesis of A<sub>1-x</sub>A′<sub>x</sub>NbO<sub>3</sub> (A = Na<sup>+</sup>, K<sup>+</sup>; A′ = La<sup>3+</sup>, Sr<sup>2+</sup>) and its electrical properties」の研究トピックを掘り下げます。これらがまとまってユニークなフィンガープリントを構成します。

引用スタイル