Synthesis of poly(3,4-azopyridylene) and oxygen-binding affinity of its complex with cobaltporphyrin

Bao Qing Shentu*, Zhi Xue Weng, Hiroyuki Nishide

*この研究の対応する著者

研究成果査読

抄録

Synthesis and characteristics of poly(3,4-azopyridylene) (PAP), conductivity and oxygen-binding affinity of its complex with meso-α,α,α,α-tetrakis(o-pivalamidophenyl) porphyrinatocobalt(II) (CoP) were studied. PAP was prepared by oxidative polymerization of 3,4-diaminopyridine (DAP) in DMF solution using CuCl/pyridine as the catalyst. IR and NMR results showed that the peak of amido group in DAP was converted to the azo group in PAP and a π conjugated polymer was synthesized. The average molecular weight of PAP was determined to be 5.0 × 103. The PAP-CoP complex was prepared by complexing the pyridyl group of PAP with the fifth coordination site of CoP in DMF solution. In comparison with the CoP complex with a non-π conjugated polymer, the PAP-CoP complex shows good electroconductivity of 5.8 × 10-6 S cm-1. The PAP-CoP complex displays a reversible change in the UV-Visible absorption spectrum from the deoxy form to the oxy or oxygen-binding one with an isosbestic point, in response to the partial oxygen pressure of the atmosphere. The oxygen-response behavior was monitored at the absorbance ascribed to the oxy form at 548 nm to give the oxygen-binding affinity. The oxygen-binding equilibrium curves of PAP-CoP complex obey a Langmuir isotherm. DMF has great effects on the oxygen-binding properties of the PAP-CoP complex. The oxygen-binding affinity of PAP-CoP complex in the solid state is higher than that in DMF solution. With decreasing temperature, the oxygen-binding affinity of the PAP-CoP complex increases.

本文言語English
ページ(範囲)417-422
ページ数6
ジャーナルChinese Journal of Polymer Science (English Edition)
23
4
DOI
出版ステータスPublished - 2005 7

ASJC Scopus subject areas

  • ポリマーおよびプラスチック
  • 材料化学

フィンガープリント

「Synthesis of poly(3,4-azopyridylene) and oxygen-binding affinity of its complex with cobaltporphyrin」の研究トピックを掘り下げます。これらがまとまってユニークなフィンガープリントを構成します。

引用スタイル