Synthesis of ternary compound sulfide nanoparticles

Sayako Hamaguchi*, Takuma Yamamoto, Masakazu Kobayashi

*この研究の対応する著者

研究成果: Article査読

4 被引用数 (Scopus)

抄録

Conventional phosphor materials are doped ternary or quaternary compounds; hence it would be difficult to prepare those nanoparticles by build up methods. Ba2ZnS3:Mn, SrGa2S4:Eu, and BaAl2S4:Eu nanoparticles were prepared by a break down method, namely ball-milling method. Transmission electron microscopy (TEM), and TEM-energy-dispersive X-ray spectroscopy (EDX) measurements showed several-nanometer-size stoichiometric and dispersed nanoparticles were achieved. The annealing was performed after the milling for those particles to cure the mechanical damages. The annealing in a vacuum at around the calcination temperature of starting materials showed the cured photoluminescence (PL). ZnO-coating was performed and the uniform coating layer of the thickness about 10nm was formed on the phosphor nanoparticles. The ZnO-coated nanoparticles exhibited an improved stability in PL.

本文言語English
論文番号04C131
ジャーナルJapanese journal of applied physics
48
4 PART 2
DOI
出版ステータスPublished - 2009 4

ASJC Scopus subject areas

  • 工学(全般)
  • 物理学および天文学(全般)

フィンガープリント

「Synthesis of ternary compound sulfide nanoparticles」の研究トピックを掘り下げます。これらがまとまってユニークなフィンガープリントを構成します。

引用スタイル