Tailoring Ti3SiC2 ceramic via a strong magnetic field alignment method followed by spark plasma sintering

Chunfeng Hu, Yoshio Sakka, Salvatore Grasso, Tohru Suzuki, Hidehiko Tanaka

研究成果: Article

30 引用 (Scopus)

抜粋

Highly textured Ti3SiC2 ceramic was successfully fabricated by slip casting in a 12 T strong magnetic field followed by spark plasma sintering. The optimized suspension parameters for slip casting were determined as 20 vol% Ti3SiC2 and 1.5 wt% polyethyleneimine dispersant of powder in deionized water. After texturing in the 12 T strong magnetic field and then cold isostatic pressing, the relative densities of green bodies were 51.4% and 63.8%, respectively. X-ray diffraction analysis revealed that the preferred orientation of Ti3SiC 2 grains perpendicular to the magnetic field direction was along the c-axis. After sintering at 1100° and 1000°C under the pressure of 120 and 500 MPa, respectively, the relative density of Ti3SiC2 reached 88.2% and 98.6%. The Lotgering orientation factors on the textured top surface and textured side surface were determined as f(00l)=0.95 and f(hk0)=0.31, respectively. The textured microstructure contributed to the anisotropic mechanical property tested by Vickers indentation.

元の言語English
ページ(範囲)742-748
ページ数7
ジャーナルJournal of the American Ceramic Society
94
発行部数3
DOI
出版物ステータスPublished - 2011 3 1
外部発表Yes

ASJC Scopus subject areas

  • Ceramics and Composites
  • Materials Chemistry

フィンガープリント Tailoring Ti<sub>3</sub>SiC<sub>2</sub> ceramic via a strong magnetic field alignment method followed by spark plasma sintering' の研究トピックを掘り下げます。これらはともに一意のフィンガープリントを構成します。

  • これを引用