Tensile fracture properties of single glass fiber in cryogenic environment

Mamoru Hayakawa, Norihiko Taniguchi, Tsuyoshi Nishiwaki, Norio Hirayama, Hiroyuki Kawada*

*この研究の対応する著者

研究成果査読

2 被引用数 (Scopus)

抄録

The strengthening mechanism of the glass-fiber at cryogenic temperature has not been fully studied so far. In the present study, tensile tests of a single E-glass fiber with heat treatment in air and liquid nitrogen were conducted to reveal the strengthening mechanism. The strength of glass fiber in liquid nitrogen was twice as high as the strength in air. Based on the area of the mirror zone in the fracture surface, the mirror constant was detemined. Besides, the mirror constant of the glass fiber were equal regardless of the heat treatment condition and the testing temperature. From the observation of surface crack, it was clarified that the mirror zone was the mark of surface flaw propagation and therefore it was suggested that the area of mirror zone doesn't have a direct effect on fiber strength.

本文言語English
ページ(範囲)652-654
ページ数3
ジャーナルNihon Kikai Gakkai Ronbunshu, A Hen/Transactions of the Japan Society of Mechanical Engineers, Part A
76
766
DOI
出版ステータスPublished - 2010 6

ASJC Scopus subject areas

  • 材料科学(全般)
  • 材料力学
  • 機械工学

フィンガープリント

「Tensile fracture properties of single glass fiber in cryogenic environment」の研究トピックを掘り下げます。これらがまとまってユニークなフィンガープリントを構成します。

引用スタイル