The Effect of Varying Ca-Content on the Structure of High-TC Superconductor (CaxLa1-x)(Ba1.75-xLa 0.25+x)Cu3O7-δ (x = 0.5, 0.6, and 0.8) Studied by Neutron Powder Diffraction

Yasushi Sato, Markus Valkeapää, Valery Petrykin, Minoru Osada, Sten Eriksson, Masato Kakihana, Håkan Rundlöf

研究成果: Article

抄録

We have performed neutron powder diffraction (NPD) experiments on polycrystalline powders with nominal compositions (Ca0.5La 0.5)(Ba1.25La0.75)Cu3O 7-δ, (Ca0.6La0.4)(Ba 1.15La0.85)Cu3O7-δ and (Ca0.8La0.2)(Ba0.95La1.05)Cu 3O7-δ. The diffraction patterns, analysed by the Rietveld method, show that all samples consist mainly of a tetragonal Y-123 type phase. Unit cell parameters a and c shorten as the calcium content increases: a = 3.8660(2), 3.8634(3), and 3.8624(5) Å; c = 11.6325(11), 11.6143(14), and 11.5822(20) Å for x-values 0.5, 0.6, and 0.8, respectively. For the x = 0.6 and 0.8 samples the Rietveld refinement of calcium occupancies and EDX analysis suggest that the actual composition is closer to x ≈ 0.5. However, since the lattice parameters do change, it is also suggested that at these higher doping levels calcium does enter the Y-site to a larger extent than for the x = 0.5 composition. This is also in accordance with previously reported values for the Tc, which decreases slighty as x changes from 0.5 to 0.6 and has a pronounced change from 80 K to 73 K for x = 0.6 and 0.8, respectively.

元の言語English
ページ(範囲)361-364
ページ数4
ジャーナルMaterials Science Forum
443-444
出版物ステータスPublished - 2004
外部発表Yes

ASJC Scopus subject areas

  • Materials Science(all)

フィンガープリント 「The Effect of Varying Ca-Content on the Structure of High-T<sub>C</sub> Superconductor (Ca<sub>x</sub>La<sub>1-x</sub>)(Ba<sub>1.75-x</sub>La <sub>0.25+x</sub>)Cu<sub>3</sub>O<sub>7-δ</sub> (x = 0.5, 0.6, and 0.8) Studied by Neutron Powder Diffraction」の研究トピックを掘り下げます。これらがまとまってユニークなフィンガープリントを構成します。

引用スタイル