The model experiment on the formation of 2CaO SiO2-3CaO · P2O5 phase in the dephosphorization slag

Masayuki Kami*, Masahiro Terasawa, Atsushi Matsumoto, I. T.O. Kimihisa


研究成果: Article査読

7 被引用数 (Scopus)


The formation of the Ca2SiO4-Ca3P 2O8 phase in a hot metal dephosphorization slag was investigated. The reaction of a P2O5-containing slag with a solid porous CaO was observed at 1673 K by using a hot thermo-couple method. A CaO-FeO layer was formed near the interface, and next to it a solid solution of Ca2SiO4-Ca3P2O8 containing FeO was observed. The results could be explained in terms of the model proposed by Hamano et al. The Fe-P-Si alloy was reacted with dicalcium ferrite at 1673K, and the samples were analyzed by XMA. The phosphorus concentrated phases were observed near the slag-metal interface. Their compositions could be approximated as 2(CaO+FeO) -SiO23(CaO+FeO)- P2O5 and their FeO concentration decreased as the progress of the reaction.

ジャーナルTetsu-To-Hagane/Journal of the Iron and Steel Institute of Japan
出版ステータスPublished - 2009

ASJC Scopus subject areas

  • 凝縮系物理学
  • 物理化学および理論化学
  • 金属および合金
  • 材料化学


「The model experiment on the formation of 2CaO SiO<sub>2</sub>-3CaO · P<sub>2</sub>O<sub>5</sub> phase in the dephosphorization slag」の研究トピックを掘り下げます。これらがまとまってユニークなフィンガープリントを構成します。