Thermal cycling and hot-corrosion behaviors of plasma sprayed segmented thermal barrier coatings

Hongbo Guo, Hideyuki Murakami, Seiji Kuroda

研究成果: Conference contribution

4 引用 (Scopus)

抄録

Modified zirconia thermal barrier coatings (TBCs) with segmentation cracks were sprayed onto a TMS 82+ single crystalline substrate. The thermal cycling lifetime of the modified TBC was improved by 10 times compared to that of the traditional non-segmented TBC. Also, the modified coating showed much better resistance to high temperature cyclic hot-corrosion.

元の言語English
ホスト出版物のタイトルProgress in Light Metals, Aerospace Materials and Superconductors
ページ1713-1716
ページ数4
エディションPART 3
出版物ステータスPublished - 2007 12 1
外部発表Yes
イベント2006 Beijing International Materials Week, 2006 BIMW -International Conference on Aerospace Materials, ICAM 2006 - Beijing, China
継続期間: 2006 6 252006 6 30

出版物シリーズ

名前Materials Science Forum
番号PART 3
546-549
ISSN(印刷物)0255-5476

Other

Other2006 Beijing International Materials Week, 2006 BIMW -International Conference on Aerospace Materials, ICAM 2006
China
Beijing
期間06/6/2506/6/30

Fingerprint

Thermal barrier coatings
Sprayed coatings
Thermal cycling
Corrosion
Plasmas
Zirconia
Crystalline materials
Cracks
Coatings
Substrates
Temperature

ASJC Scopus subject areas

  • Materials Science(all)

これを引用

Guo, H., Murakami, H., & Kuroda, S. (2007). Thermal cycling and hot-corrosion behaviors of plasma sprayed segmented thermal barrier coatings. : Progress in Light Metals, Aerospace Materials and Superconductors (PART 3 版, pp. 1713-1716). (Materials Science Forum; 巻数 546-549, 番号 PART 3).

Thermal cycling and hot-corrosion behaviors of plasma sprayed segmented thermal barrier coatings. / Guo, Hongbo; Murakami, Hideyuki; Kuroda, Seiji.

Progress in Light Metals, Aerospace Materials and Superconductors. PART 3. 編 2007. p. 1713-1716 (Materials Science Forum; 巻 546-549, 番号 PART 3).

研究成果: Conference contribution

Guo, H, Murakami, H & Kuroda, S 2007, Thermal cycling and hot-corrosion behaviors of plasma sprayed segmented thermal barrier coatings. : Progress in Light Metals, Aerospace Materials and Superconductors. PART 3 Edn, Materials Science Forum, 番号 PART 3, 巻. 546-549, pp. 1713-1716, 2006 Beijing International Materials Week, 2006 BIMW -International Conference on Aerospace Materials, ICAM 2006, Beijing, China, 06/6/25.
Guo H, Murakami H, Kuroda S. Thermal cycling and hot-corrosion behaviors of plasma sprayed segmented thermal barrier coatings. : Progress in Light Metals, Aerospace Materials and Superconductors. PART 3 版 2007. p. 1713-1716. (Materials Science Forum; PART 3).
Guo, Hongbo ; Murakami, Hideyuki ; Kuroda, Seiji. / Thermal cycling and hot-corrosion behaviors of plasma sprayed segmented thermal barrier coatings. Progress in Light Metals, Aerospace Materials and Superconductors. PART 3. 版 2007. pp. 1713-1716 (Materials Science Forum; PART 3).
@inproceedings{33db22d295d24dc2b52433d3b3388fb3,
title = "Thermal cycling and hot-corrosion behaviors of plasma sprayed segmented thermal barrier coatings",
abstract = "Modified zirconia thermal barrier coatings (TBCs) with segmentation cracks were sprayed onto a TMS 82+ single crystalline substrate. The thermal cycling lifetime of the modified TBC was improved by 10 times compared to that of the traditional non-segmented TBC. Also, the modified coating showed much better resistance to high temperature cyclic hot-corrosion.",
keywords = "Hot corrosion, Segmentation cracks, Thermal barrier coatings (TBCs), Thermal cycling",
author = "Hongbo Guo and Hideyuki Murakami and Seiji Kuroda",
year = "2007",
month = "12",
day = "1",
language = "English",
isbn = "0878494324",
series = "Materials Science Forum",
number = "PART 3",
pages = "1713--1716",
booktitle = "Progress in Light Metals, Aerospace Materials and Superconductors",
edition = "PART 3",

}

TY - GEN

T1 - Thermal cycling and hot-corrosion behaviors of plasma sprayed segmented thermal barrier coatings

AU - Guo, Hongbo

AU - Murakami, Hideyuki

AU - Kuroda, Seiji

PY - 2007/12/1

Y1 - 2007/12/1

N2 - Modified zirconia thermal barrier coatings (TBCs) with segmentation cracks were sprayed onto a TMS 82+ single crystalline substrate. The thermal cycling lifetime of the modified TBC was improved by 10 times compared to that of the traditional non-segmented TBC. Also, the modified coating showed much better resistance to high temperature cyclic hot-corrosion.

AB - Modified zirconia thermal barrier coatings (TBCs) with segmentation cracks were sprayed onto a TMS 82+ single crystalline substrate. The thermal cycling lifetime of the modified TBC was improved by 10 times compared to that of the traditional non-segmented TBC. Also, the modified coating showed much better resistance to high temperature cyclic hot-corrosion.

KW - Hot corrosion

KW - Segmentation cracks

KW - Thermal barrier coatings (TBCs)

KW - Thermal cycling

UR - http://www.scopus.com/inward/record.url?scp=38349086363&partnerID=8YFLogxK

UR - http://www.scopus.com/inward/citedby.url?scp=38349086363&partnerID=8YFLogxK

M3 - Conference contribution

AN - SCOPUS:38349086363

SN - 0878494324

SN - 9780878494323

T3 - Materials Science Forum

SP - 1713

EP - 1716

BT - Progress in Light Metals, Aerospace Materials and Superconductors

ER -