T1 - Thermodynamic investigation of liquid Ga-As and In-As systems by the use of a drop-calorimeter
AU - Yamaguchi, Katsunori
AU - Itagaki, Kimio
AU - Yazawa, Akira
PY - 1988/10/1
Y1 - 1988/10/1
N2 - Heat contents of the Ga-As and In-As systems were measured by a drop-calorimeter in the concentration ranges of NAs=0.05 to 0.05 (GaAs, InAs) and in the respective temperature ranges of 800 t 1550 K and 700 to 1500 K. The corresponding results are illustrated in (HTH298.15)-temperature-composition ternary diagrams. The activities and heats and entropies of mixing were determined at temperature above 1200 K. The activities of Ga and In in both liquid systems showed a large negative deviation from Raoult's law at the compound side and a slight positive deviation in the Ga-rich and In-rich regions. Those of As showed a large negative deviation from Raoult's law. Based on the obtained thermodynamic data, partial pressure-temperature-composition correlation diagrams were constructed. Total pressure of arsenic gas species and partial pressure of As, showed a drastic increase with increasing temperature and arsenic concentration.
AB - Heat contents of the Ga-As and In-As systems were measured by a drop-calorimeter in the concentration ranges of NAs=0.05 to 0.05 (GaAs, InAs) and in the respective temperature ranges of 800 t 1550 K and 700 to 1500 K. The corresponding results are illustrated in (HTH298.15)-temperature-composition ternary diagrams. The activities and heats and entropies of mixing were determined at temperature above 1200 K. The activities of Ga and In in both liquid systems showed a large negative deviation from Raoult's law at the compound side and a slight positive deviation in the Ga-rich and In-rich regions. Those of As showed a large negative deviation from Raoult's law. Based on the obtained thermodynamic data, partial pressure-temperature-composition correlation diagrams were constructed. Total pressure of arsenic gas species and partial pressure of As, showed a drastic increase with increasing temperature and arsenic concentration.
UR - http://www.scopus.com/inward/record.url?scp=0024088717&partnerID=8YFLogxK
UR - http://www.scopus.com/inward/citedby.url?scp=0024088717&partnerID=8YFLogxK
M3 - Article
AN - SCOPUS:0024088717
VL - 52
SP - 966
EP - 972
JO - Nippon Kinzoku Gakkaishi/Journal of the Japan Institute of Metals
JF - Nippon Kinzoku Gakkaishi/Journal of the Japan Institute of Metals
SN - 0021-4876
IS - 10
ER -