Thermoelectric properties of sintered and textured Nd-substituted Ca 3Co4O9 ceramics

Marlène Prevel, Eddula Sudhakar Reddy, Olivier Perez, Wataru Kobayashi, Ichiro Terasaki, Christophe Goupil, Jacques Guillaume Noudem

    研究成果: Article

    45 引用 (Scopus)

    抜粋

    We present the results of low- and high-temperature measurements, from 5 to 800K, of the electrical resistivity and thermoelectric power of polycrystalline and c-axis-oriented textured samples of Ca3-zNd2Co 4O9 (0 ≤ z ≤ 0.9). Crystallo-graphic structure, microstructure and texture analyses of the samples have also been carried out. The substitution of the lighter rare-earth large ionic Nd for Ca results in an increase in the Seebeck coefficient. However, the resistivity of the samples also increases accordingly. In addition, the Hall effect of the polycrystalline C3-zNd2Co4O9 sample was studied in the 50-300 K interval, This measurement showed that the variation of Seebeck coefficient and resistivity are caused by a decrease in carrier concentration with Nd content. The decomposition temperatures of the samples with Nd content were observed to increase to values beyond the melting point of Ag, the technically important contact material for the fabrication of thermoelectric modules. The studies on the thermoforged samples indicate that the electrical resistivity of the textured samples decreased by 2.5-fold as compared with that of the conventional sintered samples. The increase in the decomposition temperature and the high Seebeck coefficient with low resistivity in thermoforged samples make the Nd-doped C3Co4O9 oxide as one of the candidate materials for high-temperature thermoelectric modules.

    元の言語English
    ページ(範囲)6533-6538
    ページ数6
    ジャーナルJapanese Journal of Applied Physics, Part 1: Regular Papers and Short Notes and Review Papers
    46
    発行部数10 A
    DOI
    出版物ステータスPublished - 2007 10 9

    ASJC Scopus subject areas

    • Physics and Astronomy (miscellaneous)

    フィンガープリント Thermoelectric properties of sintered and textured Nd-substituted Ca <sub>3</sub>Co<sub>4</sub>O<sub>9</sub> ceramics' の研究トピックを掘り下げます。これらはともに一意のフィンガープリントを構成します。

  • これを引用