Transmission electron microscopy investigation of CoFeB/MgO/CoFeB pseudospin valves annealed at different temperatures

S. V. Karthik, Y. K. Takahashi, T. Ohkubo, K. Hono, S. Ikeda, H. Ohno

研究成果: Article査読

73 被引用数 (Scopus)

抄録

We have investigated the microstructure and local chemistry of Ta/Ru/Ta/CoFeB/MgO/CoFeB/Ta/Ru magnetic tunnel junctions with different values of tunneling magnetoresistance (TMR) as a result of annealing at different temperatures. Annealing at 500 °C led to the templated crystallization of the amorphous CoFeB layer having coherent interfaces with MgO grains with an orientation relationship of 〈 001 〉 [011]MgO∥ 〈 001 〉 [001]CoFe, and the B rejected from crystallized CoFeB was found to be dissolved in upper amorphous Ta layers and segregated in the bottom crystalline Ta layer. Annealing at 600 °C led to the dissolution of 3-4 at. % Ta in the MgO barrier, and B was found to be segregated at the CoFeB/MgO and Ta/Ru interfaces as a result of the crystallization of the top amorphous Ta layer. Further degradation in TMR of the samples annealed at 650 °C results from the loss of bcc-CoFe (001) texture in the bottom CoFeB electrode due to the pronounced Ta diffusion into the CoFe/MgO/CoFe layers.

本文言語English
論文番号023920
ジャーナルJournal of Applied Physics
106
2
DOI
出版ステータスPublished - 2009
外部発表はい

ASJC Scopus subject areas

  • 物理学および天文学(全般)

フィンガープリント

「Transmission electron microscopy investigation of CoFeB/MgO/CoFeB pseudospin valves annealed at different temperatures」の研究トピックを掘り下げます。これらがまとまってユニークなフィンガープリントを構成します。

引用スタイル