Two routes to polycrystalline CoSi 2 thin films by co-sputtering Co and Si

Yukie Tsuji, Yoshiko Tsuji, Shinichi Nakamura, Suguru Noda

研究成果: Article査読

2 被引用数 (Scopus)

抄録

Two processes for the fabrication of polycrystalline CoSi 2 thin films based on the codeposition of Co and Si by sputtering were studied and compared. The first process involved "annealing after deposition", where Co and Si are codeposited at ambient temperature and then crystallized by annealing. This process yielded randomly oriented plate-like CoSi 2 grains with a grain size that is governed by the nanostructure of the as-deposited film. Polycrystalline CoSi 2 thin films were obtained at a process temperature of 170 °C, which was much lower than the annealing temperature of 500 °C needed for Co/Si bilayers. The second process involved "heating during deposition", where Co and Si are codeposited on heated substrates. This process yielded CoSi 2 grains with a columnar structure, and the grain size and degree of (1 1 1) orientation are temperature dependent. The sheet resistance of the resulting films was determined by the preparation temperature regardless of the deposition process used, i.e. "annealing after deposition" or "heating during deposition". Temperatures of 500 °C and higher were needed to achieve CoSi 2 resistivity of 40 μΩ cm or lower for both processes.

本文言語English
ページ(範囲)7118-7124
ページ数7
ジャーナルApplied Surface Science
256
23
DOI
出版ステータスPublished - 2010 9 15
外部発表はい

ASJC Scopus subject areas

  • Chemistry(all)
  • Condensed Matter Physics
  • Physics and Astronomy(all)
  • Surfaces and Interfaces
  • Surfaces, Coatings and Films

フィンガープリント 「Two routes to polycrystalline CoSi <sub>2</sub> thin films by co-sputtering Co and Si」の研究トピックを掘り下げます。これらがまとまってユニークなフィンガープリントを構成します。

引用スタイル