Very high-cycle fatigue characteristics of cross-ply CFRP laminates in transverse crack initiation

Atsushi Hosoi, Takuro Suzuki, Kensuke Kosugi, Takeru Atsumi, Yoshinobu Shimamura, Terumasa Tsuda, Hiroyuki Kawada

研究成果: Conference contribution

抄録

Fan blades are subjected to very high-cycle loadings during the design life, so it is essential to evaluate the giga-cycle fatigue characteristics of carbon fiber reinforced plastic (CFRP) laminates. In this study, the transverse crack initiation of the cross-ply CFRP laminates in very high-cycle fatigue region was evaluated using an ultrasonic fatigue testing machine. The fatigue tests were conducted at the frequency of f = 20 kHz and the stress ratio of R = −1. In order to suppress temperature rise of the specimen, the intermittent operation with the loading time of 200 ms and the dwelling time of 2000 ms was adopted. The fatigue life data to transverse crack initiation in very high-cycle fatigue region was compared with the data of the fatigue test which was conducted at the frequency of f = 5 Hz and the stress ratios of R = 0.1 and −1 using a hydraulic control fatigue test machine. It was evaluated considering the influences of the stress ratio and the thermal residual stress by using the modified Walker model. The fatigue life to the transverse crack initiation of the cross-ply CFRP laminates in the very high-cycle region exceeding 108 cycles was on the extension of the test data in the low cycle region.

元の言語English
ホスト出版物のタイトルICAF 2019 – Structural Integrity in the Age of Additive Manufacturing - Proceedings of the 30th Symposium of the International Committee on Aeronautical Fatigue, 2019
編集者Jerzy Komorowski, Antoni Niepokolczycki
出版者Springer
ページ838-846
ページ数9
ISBN(印刷物)9783030215026
DOI
出版物ステータスPublished - 2020 1 1
イベント30th Symposium of the International Committee on Aeronautical Fatigue, ICAF 2019 - Warsaw, Poland
継続期間: 2019 6 22019 6 7

出版物シリーズ

名前Lecture Notes in Mechanical Engineering
ISSN(印刷物)2195-4356
ISSN(電子版)2195-4364

Conference

Conference30th Symposium of the International Committee on Aeronautical Fatigue, ICAF 2019
Poland
Warsaw
期間19/6/219/6/7

Fingerprint

Plastic laminates
Carbon fiber reinforced plastics
Crack initiation
Fatigue of materials
Fatigue testing
carbon fiber reinforced plastic
Thermal stress
Fans
Residual stresses
Ultrasonics
Hydraulics

ASJC Scopus subject areas

  • Automotive Engineering
  • Aerospace Engineering
  • Mechanical Engineering
  • Fluid Flow and Transfer Processes

これを引用

Hosoi, A., Suzuki, T., Kosugi, K., Atsumi, T., Shimamura, Y., Tsuda, T., & Kawada, H. (2020). Very high-cycle fatigue characteristics of cross-ply CFRP laminates in transverse crack initiation. : J. Komorowski, & A. Niepokolczycki (版), ICAF 2019 – Structural Integrity in the Age of Additive Manufacturing - Proceedings of the 30th Symposium of the International Committee on Aeronautical Fatigue, 2019 (pp. 838-846). (Lecture Notes in Mechanical Engineering). Springer. https://doi.org/10.1007/978-3-030-21503-3_66

Very high-cycle fatigue characteristics of cross-ply CFRP laminates in transverse crack initiation. / Hosoi, Atsushi; Suzuki, Takuro; Kosugi, Kensuke; Atsumi, Takeru; Shimamura, Yoshinobu; Tsuda, Terumasa; Kawada, Hiroyuki.

ICAF 2019 – Structural Integrity in the Age of Additive Manufacturing - Proceedings of the 30th Symposium of the International Committee on Aeronautical Fatigue, 2019. 版 / Jerzy Komorowski; Antoni Niepokolczycki. Springer, 2020. p. 838-846 (Lecture Notes in Mechanical Engineering).

研究成果: Conference contribution

Hosoi, A, Suzuki, T, Kosugi, K, Atsumi, T, Shimamura, Y, Tsuda, T & Kawada, H 2020, Very high-cycle fatigue characteristics of cross-ply CFRP laminates in transverse crack initiation. : J Komorowski & A Niepokolczycki (版), ICAF 2019 – Structural Integrity in the Age of Additive Manufacturing - Proceedings of the 30th Symposium of the International Committee on Aeronautical Fatigue, 2019. Lecture Notes in Mechanical Engineering, Springer, pp. 838-846, 30th Symposium of the International Committee on Aeronautical Fatigue, ICAF 2019, Warsaw, Poland, 19/6/2. https://doi.org/10.1007/978-3-030-21503-3_66
Hosoi A, Suzuki T, Kosugi K, Atsumi T, Shimamura Y, Tsuda T その他. Very high-cycle fatigue characteristics of cross-ply CFRP laminates in transverse crack initiation. : Komorowski J, Niepokolczycki A, 編集者, ICAF 2019 – Structural Integrity in the Age of Additive Manufacturing - Proceedings of the 30th Symposium of the International Committee on Aeronautical Fatigue, 2019. Springer. 2020. p. 838-846. (Lecture Notes in Mechanical Engineering). https://doi.org/10.1007/978-3-030-21503-3_66
Hosoi, Atsushi ; Suzuki, Takuro ; Kosugi, Kensuke ; Atsumi, Takeru ; Shimamura, Yoshinobu ; Tsuda, Terumasa ; Kawada, Hiroyuki. / Very high-cycle fatigue characteristics of cross-ply CFRP laminates in transverse crack initiation. ICAF 2019 – Structural Integrity in the Age of Additive Manufacturing - Proceedings of the 30th Symposium of the International Committee on Aeronautical Fatigue, 2019. 編集者 / Jerzy Komorowski ; Antoni Niepokolczycki. Springer, 2020. pp. 838-846 (Lecture Notes in Mechanical Engineering).
@inproceedings{a0b209e909f845a9b70016fecd3003e8,
title = "Very high-cycle fatigue characteristics of cross-ply CFRP laminates in transverse crack initiation",
abstract = "Fan blades are subjected to very high-cycle loadings during the design life, so it is essential to evaluate the giga-cycle fatigue characteristics of carbon fiber reinforced plastic (CFRP) laminates. In this study, the transverse crack initiation of the cross-ply CFRP laminates in very high-cycle fatigue region was evaluated using an ultrasonic fatigue testing machine. The fatigue tests were conducted at the frequency of f = 20 kHz and the stress ratio of R = −1. In order to suppress temperature rise of the specimen, the intermittent operation with the loading time of 200 ms and the dwelling time of 2000 ms was adopted. The fatigue life data to transverse crack initiation in very high-cycle fatigue region was compared with the data of the fatigue test which was conducted at the frequency of f = 5 Hz and the stress ratios of R = 0.1 and −1 using a hydraulic control fatigue test machine. It was evaluated considering the influences of the stress ratio and the thermal residual stress by using the modified Walker model. The fatigue life to the transverse crack initiation of the cross-ply CFRP laminates in the very high-cycle region exceeding 108 cycles was on the extension of the test data in the low cycle region.",
keywords = "CFRP, Giga-cycle fatigue, Transverse crack, Ultrasonic",
author = "Atsushi Hosoi and Takuro Suzuki and Kensuke Kosugi and Takeru Atsumi and Yoshinobu Shimamura and Terumasa Tsuda and Hiroyuki Kawada",
year = "2020",
month = "1",
day = "1",
doi = "10.1007/978-3-030-21503-3_66",
language = "English",
isbn = "9783030215026",
series = "Lecture Notes in Mechanical Engineering",
publisher = "Springer",
pages = "838--846",
editor = "Jerzy Komorowski and Antoni Niepokolczycki",
booktitle = "ICAF 2019 – Structural Integrity in the Age of Additive Manufacturing - Proceedings of the 30th Symposium of the International Committee on Aeronautical Fatigue, 2019",

}

TY - GEN

T1 - Very high-cycle fatigue characteristics of cross-ply CFRP laminates in transverse crack initiation

AU - Hosoi, Atsushi

AU - Suzuki, Takuro

AU - Kosugi, Kensuke

AU - Atsumi, Takeru

AU - Shimamura, Yoshinobu

AU - Tsuda, Terumasa

AU - Kawada, Hiroyuki

PY - 2020/1/1

Y1 - 2020/1/1

N2 - Fan blades are subjected to very high-cycle loadings during the design life, so it is essential to evaluate the giga-cycle fatigue characteristics of carbon fiber reinforced plastic (CFRP) laminates. In this study, the transverse crack initiation of the cross-ply CFRP laminates in very high-cycle fatigue region was evaluated using an ultrasonic fatigue testing machine. The fatigue tests were conducted at the frequency of f = 20 kHz and the stress ratio of R = −1. In order to suppress temperature rise of the specimen, the intermittent operation with the loading time of 200 ms and the dwelling time of 2000 ms was adopted. The fatigue life data to transverse crack initiation in very high-cycle fatigue region was compared with the data of the fatigue test which was conducted at the frequency of f = 5 Hz and the stress ratios of R = 0.1 and −1 using a hydraulic control fatigue test machine. It was evaluated considering the influences of the stress ratio and the thermal residual stress by using the modified Walker model. The fatigue life to the transverse crack initiation of the cross-ply CFRP laminates in the very high-cycle region exceeding 108 cycles was on the extension of the test data in the low cycle region.

AB - Fan blades are subjected to very high-cycle loadings during the design life, so it is essential to evaluate the giga-cycle fatigue characteristics of carbon fiber reinforced plastic (CFRP) laminates. In this study, the transverse crack initiation of the cross-ply CFRP laminates in very high-cycle fatigue region was evaluated using an ultrasonic fatigue testing machine. The fatigue tests were conducted at the frequency of f = 20 kHz and the stress ratio of R = −1. In order to suppress temperature rise of the specimen, the intermittent operation with the loading time of 200 ms and the dwelling time of 2000 ms was adopted. The fatigue life data to transverse crack initiation in very high-cycle fatigue region was compared with the data of the fatigue test which was conducted at the frequency of f = 5 Hz and the stress ratios of R = 0.1 and −1 using a hydraulic control fatigue test machine. It was evaluated considering the influences of the stress ratio and the thermal residual stress by using the modified Walker model. The fatigue life to the transverse crack initiation of the cross-ply CFRP laminates in the very high-cycle region exceeding 108 cycles was on the extension of the test data in the low cycle region.

KW - CFRP

KW - Giga-cycle fatigue

KW - Transverse crack

KW - Ultrasonic

UR - http://www.scopus.com/inward/record.url?scp=85071840159&partnerID=8YFLogxK

UR - http://www.scopus.com/inward/citedby.url?scp=85071840159&partnerID=8YFLogxK

U2 - 10.1007/978-3-030-21503-3_66

DO - 10.1007/978-3-030-21503-3_66

M3 - Conference contribution

AN - SCOPUS:85071840159

SN - 9783030215026

T3 - Lecture Notes in Mechanical Engineering

SP - 838

EP - 846

BT - ICAF 2019 – Structural Integrity in the Age of Additive Manufacturing - Proceedings of the 30th Symposium of the International Committee on Aeronautical Fatigue, 2019

A2 - Komorowski, Jerzy

A2 - Niepokolczycki, Antoni

PB - Springer

ER -